稀土防腐防污涂料的制备与性能分析-preparation and performance analysis of rare earth anti-corrosion and anti-fouling coatings.docxVIP

重庆大学硕士学位论文 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV immersion in 3.5wt% NaCl solution after 30 minutes and about 107 Ω·cm2 after 7 days. It was higher than that with untreated CeO2 and epoxy resin. The research of my paper get the results that the optimal formulation of epoxy coating: the E44 epoxy resin70 g, treated CeO2 2.5 g, SiO2 14 g, curing agent 42 g. Preferred formula preparation anti-corrosion and anti-fouling coating performance test results are as follows: the hardness of 2 H, the adhesive force on galvanized steel of one grade, the impact resistance of 50 kg·cm. Its electrochemical impedance was 108 Ω·cm2 above at immersion in 3.5wt% NaCl solution after 10 days and the contact angle of water against it to be 90 ° above, the basic and hydrophobic properties of coating are good. We also see the anti-corrosion and anti-fouling performance increasing. Keywords: epoxy coating; KH560 coupling agent; fillers modification; anti-corrosion; anti-fouling 重庆大学硕士学位论文 重庆大学硕士学位论文 目 录 目 录 中文摘要 I 英文摘要II HYPERLINK \l _bookmark0 1 绪 论 1 HYPERLINK \l _bookmark1 1.1 课题背景 1 HYPERLINK \l _bookmark2 1.2 管道的防腐与防污研究 1 HYPERLINK \l _bookmark3 1.2.1 管道防腐机理及保护措施 1 HYPERLINK \l _bookmark4 1.2.2 管道防污涂料的作用机理 4 HYPERLINK \l _bookmark5 1.3 稀土在涂料中研究进展 5 HYPERLINK \l _bookmark6 1.4 响应面法优化涂料配方 7 HYPERLINK \l _bookmark7 1.5 本课题研究意义与内容 10 HYPERLINK \l _bookmark8 1.5.1 本课题研究的意义 10 HYPERLINK \l _bookmark9 1.5.2 本课题研究的内容11 HYPERLINK \l _bookmark10 1.5.3 论文工作的创新性11 HYPERLINK \l _bookmark11 2 样品制备及性能测试研究 12 HYPERLINK \l _bookmark12 2.1 实验仪器及材料 12 HYPERLINK \l _bookmark13 2.1.1 实验仪器 12 HYPERLINK \l _bookmark14 2.1.2 实验材料 12 HYPERLINK \l _bookmark15 2.2 试样制备 16 HYPERLINK \l _bookmark16 2.2.1 稀土改性 16 HYPERLINK \l _bookmark17 2.2.2 涂料配方 16 HYPERLINK \l _bookmark18 2.2.3 涂层制备 16 HYPERLINK \l _bookmark19 2.3 涂层性能测试与表征 17 HYPERLINK \l _bookmark20 2.3.1 涂膜干燥时间 17 HYPERLINK \l _bookmark21 2.3.2 涂膜附着力测试 1