管线钢在沉积物下的腐蚀行为及有机膦缓蚀剂的作用效果-ResearchGate.PDFVIP

See discussions, stats, and aut hor profi les for t his publicat ion at : htt ps:///publicat ion/301583903 Corrosion behavior of pipeline steel under deposit corrosion and the inhibition performance of organic phosphine inhibitor Article  in  Acta Metallurgica Sinica -Chinese Edition- · March 2016 DO I: 10.11900/0412.1961.2015.00327 CITAT ION READS 1 96 6 authors, including: Y.-Z. Xu Deakin University 14 PUBLICAT IONS   23 CITAT IONS    SEE PROFILE Some of the authors of this publication are also working on these related projects: corrosion View project Plasma Polymer Surface Engineering View project A ll content following this page was uploaded by Y.-Z. Xu on 27 A ugust 2017. T he user has requested enhancement of the dow nloaded file. 第52 卷 第3 期 Vol.52 No.3 2016 年 3 月 第320-330 页 ACTA METALLURGICA SINICA Mar. 2016 pp.320-330 管线钢在沉积物下的腐蚀行为及 有机膦缓蚀剂的作用效果* 1) 1) 2) 1) 1) 3) 徐云泽 黄 一 盈 亮 杨 飞 李 兵 王晓娜 1) 大连理工大学船舶工程学院, 大连 116024 2) 大连理工大学材料科学与工程学院, 大连 116024 3) 大连理工大学物理与光电学院, 大连 116024 摘 要 利用动电位扫描(PDS), 电化学阻抗谱(EIS)和线性极化电阻法(LPR), 研究了石英砂沉积物覆盖下的X65 管线钢在 含氧盐溶液中的腐蚀行为及有机膦缓蚀剂乙二胺四亚甲基膦酸钠(EDTMPS)的作用效果. 通过丝束电极(WBE)对沉积物所 导致的电偶效应进行了测试. 结果表明, 沉积物覆盖下的X65 钢平均腐蚀速率变缓, 但伴随有局部腐蚀发生. 在溶液中加注 35 mg/L 的EDTMPS 后, 裸露的X65 钢电极的腐蚀速率在3 h 内由0.17 mm/a 降低并稳定在0.082 mm/a, 沉积物覆盖下的 X65 钢电极在6 h 内腐蚀速率由0.051 mm/a 降低到0.026 mm/a 并保持稳定, EDTMPS 对裸钢和沉积物覆盖下的碳