芯柱高性能混凝土配合比试验性研究.docVIP

芯柱高性能混凝土配合比试验性研究 　　[摘要]：本文采用地方材料，根据固定砂石体积法确定芯柱自密实混凝土初步配合比，采用不同品种外加剂合理复合，通过试验对该初步配合比进行优化，使自密实混凝土拌合物的工作性满足了施工要求，同时硬化后自密实混凝土的强度满足强度等级要求。 　　 　　[关键词]：正交试验法、低强度自密实混凝土、扩展度、高效减水剂 　　[abstract] : using local materials, according to fixed sand volume method to determine the core column of self-compacting concrete mixing preliminary, using different varieties reasonably complex admixture, through the test for the preliminary optimized mix, that of self-compacting concrete things as the workability of meet the construction requirements, at the same time, after sclerosis of self-compacting concrete strength grade of strength to meet requirements. 　　 　　[key words] : the orthogonal experiment method, low intensity of self-compacting concrete, extended degree, high efficiency water reducing agent 　　 　　中图分类号：TU37文献标识码：A 文章编号： 　　 　　1材料及试验方法 　　1.1材料 　　1.1.1水泥 　　 自密实混凝土一般选择硅酸盐水泥、普通硅酸盐水泥和矿渣硅酸盐水泥，选择水泥时应考虑与所用高效减水剂的相容性。使用时要求水泥品种和来源应相对稳定，本试验采用鼎鑫牌42.5普通硅酸盐水泥。 　　1.1.2活性矿物掺合料 　　 自密实混凝土常用的活性矿物掺合料有粉煤灰、矿渣微粉、硅灰等，掺合料不但能提高新拌混凝土的工作性，而且可以抑制混凝土拌合物的坍落度损失，本试验采用河北衡水陶城I级粉煤灰， 　　1.1.3粗集料 　　 考虑到混凝土小型承重砌块芯柱的结构特点，所用碎石最大粒径一般10mm，本试验采用满城5～10mm连续级配碎石，级配良好， 　　1.1.4细集料 　　 采用满城河砂，细度模数2.59，为中砂，级配良好。 　　1.1.5外加剂 　　保定慕湖外加剂公司研制生产的萘系（UNF-5）高效减水剂、MNC-ZC增稠剂和葡萄糖酸钠等缓凝剂， 　　1.1.6水自来水 　　1.2试验方法 　　1.2.1自密实混凝土拌合方法 　　1）人工拌合 　　2）机械拌合 　　1.2.2自密实混凝土工作性测定方法 　　1）坍落度 　　 按GBJ80-85《普通混凝土拌合物性能测试方法》标准测定坍落度，不用分层插捣。从开始装料到提坍落度筒的整个过程应不间断地进行，并应在150s内完成。通过试验认为免振捣自密实混凝土坍落度就在240mm～270mm之间较适宜。 　　2）扩展度 　　 通过试验认为免振捣自密实混凝土的扩展度≥550mm比较适宜。 　　3）中边差 　　 分别测定2个不同边缘部位有骨料地方的混凝土高度与中间混凝土最大厚度之差的平均值，中边差应控制在25mm以内为好。 　　1.2.3自密实混凝土强度的测定方法 　　1.2.3.1试件的浇筑成型 　　混凝土试件成型时，不用分层插捣，无需振动成型，将混凝土拌合物装满试模然后抹平即可。 　　1.2.3.2试件的养护 　　 试件成型后，在实验室放置一天后拆模，然后送入标准养护室至试验龄期取出。 　　1.2.3.3混凝土抗压强度测定 　　 按GBJ81-85《普通混凝土力学性能试验方法》进行。 　　2自密实混凝土配制理论及其配合参数的确定 　　2.1自密实混凝土配制理论 　　 自密实混凝土一般掺入高效减水剂来提高混凝土拌合物的流动性。当用水量和外加剂增大时，流动性随之增大，而抗离析性则随之下降。芯柱混凝土拌合物的最主要特点是高流动性同时具有高稳定性，因此，合理选择配合比参数以及不同品种外加剂复合，使自密实混凝土获得高流动性、高稳定性的平衡是芯柱混凝土配合比设计的关键。[1] 　　2.2自密实混凝土配合比参数的确定 　　 对于自密实混凝土来说