钢纤维含量对活性粉末混凝土抗疲劳性能影响.docVIP

钢纤维含量对活性粉末混凝土抗疲劳性能影响 　　摘 要：通过对3种不同钢纤维含量的活性粉末混凝土（RPC）进行单向受压等幅疲劳试验，研究了钢纤维含量对其抗疲劳性能的影响.结果表明：在疲劳荷载作用下，素RPC的破坏形态表现为劈裂破坏，钢纤维含量分别为??1.5%和3%的RPC都表现为剪切破坏.随钢纤维含量的提高，RPC的疲劳寿命和疲劳强度相应提高.其宏观损伤、ε-n/Nf曲线和疲劳变形模量的衰减均表现出3阶段规律，随钢纤维含量的提高，ε-n/Nf曲线第1阶段和第3阶段延长.对应相同的荷载循环比，疲劳变形模量随钢纤维含量的增大而显著提高.在RPC构件抗疲劳验算时，建议钢纤维含量分别为1.5%和3%时，疲劳弹性模量与初始弹性模量的比值分别取0.7和0.75. 　　关键词：疲劳性能；疲劳试验；活性粉末混凝土；钢纤维含量 　　中图分类号：TU528.572 文献标识码：A 　　 　　Fatigue Properties of Reactive Powder Concrete with?? 　　Different Steel Fiber Ratios 　　FANG Zhi1?k,XIANG Yu1,KUANG Zhen2,WANG Chang-lin3 　　 (1. College of Civil Engineering，Hunan Univ，Changsha，Hunan 410082，China；?? 　　2. Hunan Zhongda Construction Engineering Testing Technology Co, Ltd，Changsha，Hunan 410205，China；?? 　　3. The 95259 Force of Chinese PLA，Guangzhou,Guangdong 510000，China ) 　　Abstract: 　　The fatigue properties of RPC (Reactive Powder Concrete) with different steel fiber ratios of 0%, 1.5% and 3% in volume were investigated with the uniaxial compressive fatigue test. The results showed that the splitting failure mode appeared for pure RPC specimens without steel fiber, but the shear failure mode occurred for those specimens with steel fiber of 1.5% or 3% in volume. The fatigue life and strength increased with the increase of steel fiber ratio; the macroscopic damage, ε-n/N??f curves and the evolution of the fatigue deformation modulus of tested RPC experienced three stages. With the increase of steel fiber ratio, the first and third stages of ε-n/N??f curves lengthened，and the fatigue deformation modulus significantly increased with the increase of the steel fiber ratio corresponding to the same n/N??f. It is suggested that the ratio of fatigue deformation modulus to the initial elastic modulus should be 0.7 and ??0.75 for the RPC with a steel fiber ratio of 1.5% and 3%, respectively. 　　Key words:fatigue properties; fatigue test；Reactive Powder Concrete（RPC）;steel fiber ratio 　　 　　活性粉末混凝土(Reactive Powder Concrete，RPC)是一种具有高强度、高耐久性及良好韧性的超高性能混凝土，具有广阔的研究与应用前景.