硅藻土改性沥青常规性能与低温流变性能研究.docVIP

硅藻土改性沥青常规性能与低温流变性能研究 　　摘要：系统研究了不同掺量下硅藻土改性沥青的感温性、高温性能等常规性能，并进一步借助BBR试验对硅藻土改性沥青的低温流变性能进行了评价。研究发现：将硅藻土作为一种改性剂加入到沥青中，能够改善沥青的感温性、高温性能、低温性能等性能，并且当掺量为11%时，硅藻土对沥青的感温性、高温性能、低温性能改善效果均较好。 　　关键词：硅藻土改性沥青；常规性能；低温流变性能 　　Abstract: The system has a different dosage under the diatomite modified asphalt temperature susceptibility, high temperature performance and general performance, and further with the BBR tests were evaluated on the low-temperature rheological properties of the diatomite modified asphalt. The study found that: diatomaceous earth as a modifier added to asphalt to improve the performance of the asphalt temperature, high temperature performance, low-temperature performance, and when the content is 11%, diatomaceous earth sense of asphalt temperature, high temperature performance, low temperature performance improvement are good. 　　Key words: Diatomite modified asphalt; regular performance; low temperature rheological properties 　　 中图分类号：TU528.42文献标识码： A 文章编号： 　　 　　 引言 　　 随着交通量的不断增长，车辆大型化、交通渠化和超载严重化等问题导致沥青路面的车辙、开裂、剥落等病害日益严重，沥青路面的应用前景面临着严峻考验[1]。利用改性剂对沥青进行改性，以提高沥青的路用性能，能够很好的解决这一问题。改性剂分为有机和无机两类：有机改性剂，即各种聚合物改性剂如SBS、SBR、PE、EVA等；无机改性剂，如硅藻土、碳黑、硫磺、玻璃纤维、石棉以及木质纤维等[2-3]。硅藻土作为一种无机改性剂，生产工艺简单、价格低廉、性能优良、储量丰富，将其掺加到沥青中，可改善沥青及其混合料的高温稳定性、低温抗裂性，提高水稳性、抗疲劳性和抗老化性[4-5]。硅藻土改性沥青的上述优点，必将使其具有广泛的应用前景。 　　 常规试验 　　 选取9%，11%，13%，15%四个掺量（外掺）的硅藻土改性沥青，并测试其相应的针入度、软化点、延度，以评价硅藻土改性沥青的常规性能，测试结果见表3。 　　表3硅藻土改性沥青的三大指标 　　 　　 　　 　　 根据四种硅藻土改性沥青的15℃、25℃、30℃针入度，对其相关性能指标进行计算，其结果如图1、图2、图3所示。 　　2.1 感温性分析 　　 采用PI值作为硅藻土改性沥青感温性的评价指标[6]，其随掺量的变化规律如图1所示。 　　 　　 　　 　　 图1PI值随掺量的变化规律 　　 由图1可知，所有硅藻土改性沥青的PI值均大于基质沥青，说明硅藻土的加入能够改善沥青的感温性。硅藻土改性沥青的PI值随掺量的增加而略有降低，但变化不大，表明掺量对硅藻土改性沥青的感温性影响不大。 　　2.2 高温性能分析 　　 以25℃针入度，软化点和当量软化点T800作为高温性能评价指标，其随掺量的变化规律见图2中1）和2）。 　　 　　 　　 　　 1）针入度（25℃）随掺量的变化规律2）软化点与T800随掺量的变化规律 　　 图2针入度（25℃）、软化点与T800随掺量的变化规律 　　 （1）由图2中1）可以看出，硅藻土改性沥青的针入度均明显小于基质沥青，并且随着掺量增大，硅藻土改性沥青的针入度呈减小趋势，但掺量在11%~15%范围内，针入度基本相同。 　　 （2）分析图2中2）可知，硅藻土改性沥青的软化点和当量软化点T800均明显大于基质沥青，并且随着掺量增大，软化点和当量软化点T800均呈现出先增大后减小的趋势，在掺量