内蒙古 内蒙古科技大学硕士学位论文 III III occur. When the iterval time is 20s, we can discriminate the 900℃ degree centigrade as non-recrystallization region, 950℃ degree centigrade partial recrystallization, 1000℃-1050℃ degree centigrade as complete recrystallization. Multi-pass compression, the program one and two rolled in the first pass reduction at 1100℃ degree centigrade, recrystallization occurred. The second and third pass reduction are the process of accumulation of strain. The forth rolled 18 percent at 910℃ degree centigrade, There appeared recrystallization tendency.Dynamic recrystallization due to large reduction. The program three rolled at complete recrystallization region in the first and second pass reduction, the other two pass reduction rolled at non-recrystallization region, avoiding partial recrystallization region can make the grain more refined.Research found that: Bainite steel exists metallurgical defects,such as banded structure and MnS inclusions. Prone to Martensite during the cooling process, which is the cause of cracking of the rail. Key Words: Bainite rail; Recrystallization; Martensite; Bainite PAGE PAGE 1 目 录 摘 要 I Abstract II 引 言 1 1 贝氏体钢轨钢的研究背景与意义 2 1.1 钢轨的发展历史 2 1.1.1 钢轨钢级的发展 2 1.1.2 钢轨钢的材质 3 1.2 现代钢轨 3 1.2.1 国内外钢轨的现状及发展 3 1.2.2 钢轨钢的分类方法 5 1.2.3 我国钢轨钢化学成分及性能特点 9 1.3 贝氏体钢轨 10 1.3.1 贝氏体钢轨的发展概况 11 1.4 影响贝氏体钢轨性能的因素 13 1.4.1 残余奥氏体对贝氏体钢轨的影响 13 1.4.2 合金元素在贝氏体钢轨中的作用 14 1.4.3 回火工艺对贝氏体钢轨的影响 15 1.5 选题背景 16 2 研究内容及方案 18 2.1 实验材料 18 2.2 实验设备 18 2.3 实验内容 18 2.4 热处理工艺研究方案 19 2.5 热模拟研究方案 21 2.5.1 贝氏体钢轨钢动态再结晶的实验方案 21 2.5.2 贝氏体钢轨钢静态再结晶的实验方案 22 2.5.3 多道次压缩应力应变的实验方案 23 2.6 硬度检测 24 3 不同热处理工艺下贝氏体钢的组织转变 25 3.1 冷却速度对组织的影响 25 3.2 等温淬火对组织的影响 29 3.3 回火工艺对组织的影响 31 3.4 组织缺陷 32 3.5 小结 34 4 贝氏体钢热模拟的实验研究 35 4.1 贝氏体钢轨动态再结晶的实验研究 35 4.1.1 单道次热模拟应力-应变曲线分析 35 4.1.2 单道次热模拟显微组织 36 4.2 贝氏体钢轨静态再结晶的实验研究 37 4.2.1 单道次热模拟显微组织 37 4.2.2 单道次热模拟显微组织 40 4.3 多道次压下模拟的实验研究 42 4.3.1 多道次压缩应力应变曲线 42 4.3.2 多道次显微组织 43 4.4 小结 44 结 论 4