高温干湿交替环境下frp-混凝土界面粘结性能的耐久性研究-结构工程专业论文.docxVIP

哈尔滨工业大学工学硕士学位论文 哈尔滨工业大学工学硕士学位论文 - - II - Abstract Scholars and engineers have paid more and more attention on the FRP reinforced concrete technology. FRP reinforced concrete structure is usually exposed to the outside. Under the influence of corrosive environment, some problems will also restrict the development and promotion of the technology of FRP reinforced concrete, such as the structures durabil ity and how to design the durability of FRP reinforcement components. From the study of the degradation of materials (FRP, resin, concrete) to the interface bonding (performance of FRP-to-resin and FRP-to-concrete), this paper has systematically analyzed the bond performances of FRP-to-concrete under the corrosive environment of high temperature and dry-wet cycling. Main research results of this thesis are as follows. The study on the durability of materials is the basis of the research on durability of interface. Based on the mechanics and micro experiments, this paper has studied the influence of the environment of high temperature and dry-wet cycling on the degradation of the tensile properties of carbon fiber, glass fiber and resin and the compressive strength of concrete. The results showed that in 300 times of the action of high temperature and dry-wet cycling, the tensile strength of CFRP didnt go down, and elongation at break declined slightly. Compared to CFRP, the tensile strength and elongation at break of GFRP declined much more, and the elastic modulus of two kinds of FRP remained to be unchanged; the results of macroscopic and microscopic experiment showed that the post curing in the dry-wet circulation has a great influence on the mechanical properties of the resin in early phase. The compressive strength of concrete is basically no change. The good bond performance between FRP and the resin is one of the precondition to the overall performance of FRP-concrete structure. This thesis has studied the degradation of the bond performances of FRP-resin thro