纳米TiO2制备条件优化及性能的研究.docVIP

纳米TiO2制备条件优化及性能的研究 　　摘要: 以亚甲基蓝为降解物，考察了TiCl?4浓度、超声时间、水浴温度、焙烧温度、焙烧时间等制备条件对TiO?2光催化活性的影响.结果表明：TiCl?4浓度为0.50mol/L，反应前超声30min，反应后超声50min，水浴温度75℃，焙烧温度500 ℃，焙烧2h的条件下，亚甲基蓝降解率为99.35%，并与P-25做了比较，自制TiO?2粉体的性能优良.用XRD和FT-IR进行了表征，结果表明：混合晶形的TiO?2粉体的降解效果较好. 　　? 　　关键词: 纳米TiO?2；制备；亚甲基蓝；表征? 　　中图分类号:TQ 426 　　 文献标志码:A文章编号:1672-8513(2011)06-0458-04 　　?? 　　Optimization of the Preparation of Nano-TiO?2 and Its Property 　　 　　ZHANG Shi?li，LIU Man?hong，CUI Jian，WANG Hong?bin，LIU Tian?cheng 　　? 　　（Key Laboratory of Ethnic Medicine Resource Chemistry, State Ethnic Affairs Commission and Ministry of Education, ?Yunnan University of Nationalities, Kunming 650031， China） 　　 　　Abstract: This is a study on TiCl?4 concentration, ultrasonic time, water bath temperature, roasting temperature, baking time effects on the photocatalytic activity of TiO?2 by using methylene blue. The results showed that the optimization of the preparation technology of TiO?2 goes as follows: the TiCl?4 concentration is 0?5mol/L, reaction before the ultrasonic time is 30 min，reaction after the ultrasonic time is 150 min, the water bath temperature is 75℃, the roasting temperature is 500℃ and the baking time is 2h. Under this condition, the methylene blue degradation rate is 99?35%. Compared with P-25, the TiO?2 power has good properties. Using the XRD and FT-IR for characterization shows that the mixed crystal TiO?2 has better degradation efficiency. 　　? 　　Key words: nano-TiO?2; preparation; methylene blue; characterization 　　?? 　　 　　 　　 　　随着印染和人民生活水平的提高，染料污染物是目前最主要的水体污染物.具有色度深、碱度大、有机污染物含量高、水质变化大、组分复杂的特点.为了满足消费者的需求，染料产品正朝着抗光解，抗氧化，抗生物降解的方向发展，使得染料很难在自然条件下降解[1-3].长期以来，印染废水一直是工业废水处理的难点.传统的印染废水处理方法存在着处理被动、费用昂贵和易产生2次污染等缺陷.纳米TiO?2 光催化降解法具有高效、节能、安全、廉价、清洁无毒、催化范围广等优点，被越来越广泛地应用于染料废水处理等环境问题[4-8].本文作者以提高TiO?2的降解率为目标，考察了纳米TiO?2制备工艺条件.? 　　1 实验部分? 　　1.1 仪器与试剂? 　　仪器：722型分光光度计（尤尼柯上海仪器有限公司）；雷磁精密pH计（上海精密科学仪器有限公司）；8W紫外灯；8-1A磁力加热搅拌器（杭州仪表电机厂）.? 　　试剂：TiCl?4，无水乙醇，亚甲基蓝，P-25，均为分析纯.? 　　1.2 TiO?2的制备? 　　TiO?2制备按文献［9］合成，在冰水浴条件下