铸造Fe-B-C合金的组织与性能-研究.pdf

摘 要 hardness of matrix. Contrast to oil quenching, water quenching could get higher hardness but lower impact toughness. Considering hardness, impact toughness and impact grinding abrasion performance, the best modification technique is 0.2%RE+0.2%Ti and the best heat treatment technique is water quenching at 950 ℃ then air quenching at 250 ℃. At the work condition of impact load grinding abrasion, wear resistance performance of Fe-B-C alloy is decided by hardness and metallographic structure and impact toughness. The higher the hardness is, the better the wear resistance performs and the higher the stability is. However, when hardness rises to a certain degree, the wear resistance performance decreases due to that impact toughness reduces acutely. KEY WORDS: Fe-B-C alloy, microstructure, hardness, toughness, impact-grinding abrasion Dissertation Type: fundamental research IV 第1 章 前言 第1章 前 言 1.1 引 言 磨损是摩擦学研究的主要内容（摩擦、磨损、润滑）分支，是工农业生产中 普遍存在的现象，是机械设备和零件三大主要失效形式（断裂、腐蚀、磨损）之 [1, 2] 一 。磨损可造成工件频繁维修和更换，使机械设备运转效率降低；同时还可 造成机械设备所作无用功增加，导致能源消耗增加等。每年由磨损而造成的经济 损失相当惊人，据美国材料政策委员会测算，二十世纪八十年代，美国每年由于 磨损造成的经济损失约150 亿美元，前联邦德国技术科学部估测，磨损造成的损 失每年达 100 亿马克，据不完全统计，我国仅工件的磨料磨损一年就消耗钢材 150 万吨以上[3] 。磨损问题越来越引起人们的普遍重视，传统的耐磨材料自身又 存在着各种局限性，因此，开发新一代耐磨材料成为该领域科研工作者努力的方 向。 耐磨材料的发展历史悠久，种类也越来越丰富，但目前广泛应用的钢铁类耐 磨材料主要有三大类 [4, 5] ：高锰钢；合金白口铸铁；低、中合金耐磨钢及相应的 复合材料。高锰钢是一种碳含量和锰含量较高的合金钢，自从 1883 年英国人 R.A.Hadfield 发明高锰钢到现在已经有 100 多年的历史，开始时它的锰含量范围 很宽（7%~20% ），随着研究与应用的进展，逐渐找到了适宜的锰含量，即目前 国内广泛使用的成分。这种古老的钢种具有良好的塑性和韧性，但屈服强度低、 易变形，而且要在冲击力大、应力高及磨料硬的磨损条件下使用时才有很强的加 工硬化能力，表现出好的耐磨性，因此，在许多领域已经逐渐被其它的耐磨材料 所替代。普通白口铁由于不含特殊的合金元素，价格便宜是它的主要优点。但由 于它的硬度低且找不到其它的强化措施，因此仅有限的应用于不苛刻的工况条件 下。镍硬铸铁是在普通白口铁的基础上发展起来的合金白口铁，加入镍、铬等合 金元素是为了