尿素树脂系白色填料-J-Stage.PDFVIP

926 尿 素 樹 脂 系 白 色 填 料 三井東圧化学(株)化成品建材研究所 黒川 明男,鳥 居 芳典 White Filler derived from Urea Resin. Akio Kurokawa and Yoshinori Torii MITSUI TOATSU CHEMICALS, INC. Development of a new filler for paper which exhibits specific function has been expected in accordance with the trend of paper base weight reduction. A white filler derived urea resin appears on the stage as one of organic fillers. The filler is composed of porous agglomerates (average diameter ca. 5ƒÊ) comprizing from non porous spheres (average diameter 0.1-0.3ƒÊ). Agglomerates have void space of 2 cm3/g and the average void size of 0.3-0.5ƒÊ. The filler having particle size and structure explained above affords high level of light scattering (white- ness and hiding power) and absorption (opacity after printing). Keywords: Filler, Organic filler, Pigment, Organic pigment, High brightness •E Opacity •E Printing opacity, News paper, Dry strength resin 1.　は じ め に 2.　尿素樹 脂填料 の製造方法 尿素樹脂 白色順料の製造技術の研究は1966年頃チ 先ずホルムアルデ ヒド対尿素のモル比が1,0～2.0の パ ・ガイギー社(ス イス)に よって開始されたが,そ 初期縮合物を合成す る。 この初期縮合物中には,尿素 の主用途はエ ラス トマーの補強剤であった1)。1971年 樹脂填料の粒子径お よび空隙構造 をコン トロールする になって,チ バ ・ガイギー社 とキャボッ ト社(USA) ための数種の水溶性の第3成分,例 えばスチレンー無 が製紙用填料 としての応用特許 を共願 してい る。次い 水マ レイ ン酸共重合体の加水分解物,ア クリルア ミド でキャボ ッ ト社 より塗料分野3),紙加工分野4)および ーアクリロニ トリルーアク リル酸 ソーダの3元共重合 建材分野5)6)のコーテ ィング用顔料 としての用途特許 体,ア ルギン酸 ソーダ等の如 き水溶性高分子が不可欠 が出願 されている。その後は我 が国か