钒基贮氢合金的化学制备与表征材料物理与化学专业论文.docxVIP

重庆大 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV decreases from 3 cycles to 2 cycles, but the maximum hydrogen absorption capacity at 20℃ decreases from 3.63wt% to 3.47wt%; while x=0.04, alloy sample has a better overall hydrogen desorption performance with the 1.81wt% effective hydrogen desorption capacity at 40℃; all of the alloys have a good cycle stability performance. Additionally, it was studied that 10% NH4Cl was added to reaction in the firing-reduction stage. The results indicate that the alloy sample’s particle size is becoming smaller, and the hydrogen absorption kinetics performance of alloy sa