阜新恒盛国际基础大体积混凝土温度场实测与分析-建筑与土木工程专业论文.docxVIP

- - III - Glorious in advance with specific recommendations for temperature control measures and crack, and Fuxin area for future mass concrete construction to provide a reference. use HNTT-D automated temperature test system for real-time monitoring of the distribution of temperature field on the large concrete structures to prevent mass concrete foundation harmful cracks to ensure the impermeability of the Glorious foundation works in the construction process, and durability. At the same time within the concrete temperature field of the project changes in real-time monitoring data, with a high reference value. obtained by the field data and engineering simulation, the temperature changes in the goodness of fit compared to evaluate the feasibility of the proposed mass concrete temperature monitoring and conservation programs, to ensure to the ADINA simulation analysis concluded with a viable. Key Words：Mass concrete；Temperature control；Numerical simulation； The simulation analysis； - - PAGE IV - 目 录 摘 要 I Abstract II 引 言 1 1 大体积混凝土裂缝产生的机理及原因 5 1.1 大体积混凝土温度裂缝产生的机理 5 1.1.1 温度应力的形成 5 1.1.2 温度裂缝的产生 6 1.2 大体积混凝土温度裂缝产生的原因 7 1.2.1 由温度应力和温度变形造成混凝土产生裂缝 8 1.2.2 外界气温的变化使混凝土产生裂缝 8 1.2.3 混凝土干缩使混凝土产生裂缝 8 1.2.4 塑性收缩变形使混凝土产生裂缝 9 1.2.5 混凝土不均匀性使混凝土产生裂缝 9 1.2.6 设计造型使混凝土产生裂缝 9 1.3 常用混凝土温度控制和防裂措施 9 2 阜新恒盛国际大体积混凝土温度场实测 11 2.1 工程概况 11 2.1.1 混凝土配合比以及拌合物的性能 12 2.1.2 混凝土温度变化控制 13 2.2 测试目的 14 2.3 阜新恒盛国际大体积混凝土温度监测方案 14 2.3.1 测试设备及测温方法 14 2.3.2 温度监测的布置方案 16 2.4 实时监测结果分析 20 2.4.1 测温数据 20 2.4.2 数据分析 24 3 阜新恒盛国际大体积混凝土温度场数值模拟 26 3.1 大体积混凝土温度场的有限元计算原理 26 3.2 大体积混凝土的三维瞬态温度场理论 28 3.2.1 三维瞬态温度场的基本原理 28 3.2.2 温度应力的计算模型 28 3.2.3 瞬态热分析理论 29 3.3 恒盛国际大体积混凝土温度场模型的建立 30 3.3.1 建立有限元模型 30 3.3.2 建立温度场的热分析材料模型 31 3.4 恒盛国际大体积混凝土温度场的数值算法 31 3.5 对恒盛国际大体积混凝土温度场模拟结果的分析 32 3.5.1 温度场变化趋势 32 3.5.2 数值分析结果 34 3.6 本章小结 37 4 恒盛国际大体积混凝土抗裂验算 38 4.1 大体积混凝土浇筑体表面保温层厚度计算 38 4.1.1 保温材料的厚度 38 4.1.2 混凝土表面向保温介质放热的总放热系数 39 4.1.3 混凝土虚厚度 39 4.1.