AlMn中间合金对MGAlMn系合金组织及温力学性能影响的研究.docx

优秀毕业论文 精品参考文献资料 AbstractWith Abstract With the advantages of light-weight，high strength／weight ratio，superior damping capacity，recyclability et al，the application of magnesium alloys is increasing rapidly in automobiles industry．AM60 magnesium alloy is a kind of broadly used casting magnesium alloys because of its low manufacturing cost and good processing property．However，the poor high-temperature performance impedes its application scope，SO how to improve its high—temperature performance has became a subject that interested many magnesium alloy researchers． In this study two different ingredients of A1-Mn master alloys are first prepared，then adding the prepared master alloys in molten magnesium separately to prepare AM60A and AM6 1 A magnesium alloys．The rnicrostructures and phase components of prepared magnesium alloys were investigated using Optical Microscope(OM)，Scanning Electron Microscopy(SEM)with Energy Dispersive Spectrometer(EDS)，the effects of adding Ai—Mn master alloys on the mechanical properties of AM alloys were investigated by the tensile test of prepared magnesium alloys at room and l迎h temperture，the mechanism of improving the high-temperature performance of adding A1-Mn master alloys of AM alloys was investigated by analyzing the microstmctures of solution treatment and ageing treatment of prepared magnesium alloys． The results show that Mding A1-Mn master alloys can improve the morpnology and distribution of p．MglTAlt2 effectively in the microstructure ofAM alloys，reduce the amount and size of bulky eutecfic p-MglTAl 12，increase the amount of granular IB-M917A112．So the mechanical properties of magnesium alloys at room temperature have been improved obviously．Meanwhile，quicken the cooling rate Can refine the grain size of magnesium alloys．AI-Mn is a kind of high-temperature phase with thermal stability，it call he unchanged after 45 hours heat preservation at 450。C，SO adding A1·Mn II 万方数据 master master alloys can improve high—tempe