纤维增强热塑性塑料中纤维含量的精确调控.pdfVIP

纤维增强热塑性塑料中纤维含量的精确调控 王小黎　 　 汤　 炜　 　 王帮武　 　 王立峰 (航天材料及工艺研究所,北京　 100076) 文　 摘　 研究了双螺杆挤出机生产纤维增强热塑性塑料时,纤维股数、双螺杆转速、塑料喂料量与纤维含 量的关系,通过调节此三个参数,纤维含量可精确控制在±0.1wt%的范围内。 当主机螺杆转速和塑料喂料量, 或纤维股数和塑料喂料量同时增加,挤出造粒产量将提高相同倍数,而纤维含量保持不变。 本方法高效可行、 精确可控,容易为操作者所掌握,特别适用于指导生产实践。 关键词　 热塑性塑料,纤维含量,产量,调控 Precise Control of Fiber Content in Fiber Reinforced Thermoplastic Wang Xiaoli　 　 Tang Wei　 　 Wang Bangwu　 　 Wang Lifeng (Aerospace Research Institute of Materials Processing Technology,Beijing　 100076) Abstract　 The relationship among the number of skein,twin screw extruder rotating speed,adding amount of plastic and fiber contentwasstudiedintheprocessof productionoffiberreinforcedthermoplasticby twin screw extru- der. Fiber content could controlled precisely in the range of ±0.1wt% by adjusting the three parameters forward. When the twin screw extruder rotating speed and adding amount of plastic,or the number of skein and adding amount of plasticwere increased simultaneously,the output of extrusionwasimproved at the same multiple andthefiber con- tent maintained invariably. These method were efficient,feasible,accurate and controllable,and could be comprehen- ded easily by operator to direct practice. Key words　 Thermoplastic,Fiber content,Output,Control 0　 引言 始阶段要经过多次、反复的调整各项参数和试验测试 通过向热塑性塑料中添加增强纤维或对塑料进 才能满足要求,调试周期长、生产效率低、产品成本 行改性等方法制备纤维增强热塑性塑料(FRTP)是新 高。 本文通过试验探索和理论研究,以连续玻璃纤维 材料发展的一条行之有效的捷径,也是实现通用塑料 和尼龙610 为原料,采用双螺杆挤出工艺得到了玻纤 工程化、工程塑料功能化、特种工程塑料实用化的最 增强尼龙610 中玻纤含量快速、精确调控的方法,该 - [1 2] 方法降低废品率,提高设备的利用率,使产品产量最 佳技术路线 。 大部分热塑性塑料都可作为FRTP 的树脂基体,常用的增强纤维主要有玻璃纤维、碳纤 大化,同时可以迅速调整因原材料更换批次所引起的 - [3 5] 纤维