超声波化学预镀改善烧结Nd.pdf

18 8 2008 8 Vol. 18 No.8 The Chinese Journal of Nonferrous Metals Aug. 2008 1004-0609(2008)08-1512-05 Nd-Fe-B Ni-P ( 310027) Ni-PNd-Fe-B X Ni-P150 W Ni-P Nd-Fe-B Ni-P TG 174.45 A Improved adhesion of electroless Ni-P coatings on sintered Nd-Fe-B magnets by pre-plating in ultrasonic field WU Yuan-lu, YING Hua-gen, LUO Wei, YAN Mi (State Key Laboratory of Silicon Materials, Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, China) Abstract: The effects of pre-plating in ultrasonic field on the adhesion of electroless Ni-P coatings to sintered Nd-Fe-B magnets were investigated. The adhesion of Ni-P coatings to magnets with different ultrasonic power was measured by an adhesion tester. The surface and cross-sectional morphologies of the coatings were observed through SEM. The phase structure of the coatings was identified by X-ray diffraction patterns. The results show that the adhesion of Ni-P coating to Nd-Fe-B magnet was enhanced with increasing ultrasonic power. When increasing ultrasonic power up to 150 W, the adhesion strength reaches the maximum. Synchronously, a uniform and compact deposit can be obtained by pre-plating in ultrasonic field. It is suggested that the ultrasonic pre-plating contributes to the improvement of adhesion through two ways: stirring and cavitation action. Key words: sintered Nd-Fe-B magnets; electroless plating; Ni-P coatings; adhesion Nd-Fe-B [6] Ni-P Nd Nd-Fe-B [1−2] Ni-PNd-Fe-B Ni-P [3−4] Nd-Fe-BNd N