热处理对组织结构与磁致伸缩性能的影响.pdfVIP

热处理对Fe8Ga。合金组织结构与磁致伸缩性能的影响／马云庆等 ·5。 EffectsofHeat-treatmentontheM icrostructureand M agnetostrictionofFes1Ga19 MAYunqing，LAISanli，YANGShuiyuan，YANGJingjing，SHIZhan (DepartmentofMaterialsScienceandEngineering，CollegeofMaterials，XiamenUniversity，Xiamen361005) Abstract ButtoningotsofpolyerystallineFeB1Gal9alloyarepreparedbyarc-melter，andtheeffectsofdifferent heat-treatmentsontheirmicrostructureandmagnetostrictionareinvestigated．Thespecimensareannaeledat700℃ 。 800~C，and900~C，andthencooledatdifferentspeeds，i．e．quenchingintoicewater，aircooling，orfurnacecooling． Theresultsshow thatspecimensafterdifferentheat-traetmentsallexhibitsinglebccstructure，butthemagnetostric— tionsvaryfrom 34×10一 to94X 10一；Whenthehaeting temperatureis800℃，goodmagnetostriction (88×10一 ) canbeobtainedbyquenching ．Ontheotherhand，whenthespecimenisheatedatahighertemperature(900~C)，fur— nacecoo lingisabetterwaytogetgoodmagnetostriction(94×10一)．Itisspeculatedthatthehaet-traetmenttempera- tureandthecrystalorientationmaybetwoprimaryfactorsinfluencingthemagentostrictionofFeBlGa19alloy． Keywords magnetostriction， lGal9，haet-traetment 热处理对 Fe8。Ga9合金组织结构与磁致伸缩性能的影响 马云庆，赖三哩，杨水源，杨晶晶，施 展 (厦门大学材料学院材料科学与工程系，厦门 361005) 摘要 采用电弧熔炼法制备了 。Ga1。舍金多晶样品，研究了不同热处理工艺对合金组织结构及磁致伸缩性 能的影响。样品经过700℃、800℃和900℃保温后采用空冷、炉冷和淬火3种冷却方式。结果显示，经过不同热处理 后样品的微观组织均为单相bcc结构，而磁致应变从34×10 到94×1O 不等；当热处理温度为800℃时，淬火处理 后可获得较好的磁致伸缩性能(88×10 )，而热处理温度较高(900℃)时，采用炉冷的方式可获得较好的磁致伸缩性 能(94×10 )。推测热处理方式和晶体取向对Fe81Gal。合金磁致伸缩性能有较重要的影响。 关键词 磁致伸缩 Fe81Ga19 热处理 Magnetostrictivematerialsexhibitreversiblestrainsi