钢纤维和膨胀剂复合效应对喷射混凝土弯曲韧性的影响分析.pdfVIP

年第 期 混凝土与水泥制品 2012 2 2012 No.2 2 月 CHINA CONCRETE AND CEMENT PRODUCTS February 钢纤维和膨胀剂复合效应对喷射混凝土 弯曲韧性的影响分析 赵晓晶，马芹永 （安徽理工大学矿山地下工程教育部工程研究中心，淮南 232001 ） 摘 要：基于韧性在混凝土结构中的重要性，采用三分点加载的方式，探讨了膨胀剂和钢纤维的复合效应对喷 射混凝土弯曲韧性的影响规律。结果表明，当钢纤维和膨胀剂的掺量分别为 和 时，喷射补偿收缩钢纤维混凝 1.2% 8% 土的荷载 挠度曲线最为饱满；弯曲韧度指数和承载能力变化系数均大于理想弹性材料的相应值。 - 关键词：膨胀剂；钢纤维；喷射补偿收缩钢纤维混凝土；弯曲韧性 ： Abstract Based on the importance of toughness in concrete structure, using the method of three-point loading, the effecting laws of the combined effect of expansive agent and steel fiber on flexural toughness of shotcrete are discussed. The results show that the load-deflection curve of shrinkage-compensating steel fiber reinforced shotcrete is finest when the steel fiber content is 1.2% and expansive agent content is 8%. And the flexural toughness index and the coefficient of loading capacity variation are both bigger than the values of ideal elastic materials. ： Key words Expansive agent; Steel fiber; Shrinkage-compensating steel fiber reinforced shotcrete; Flexural toughness 中图分类号： 文献标识码： 文章编号： （ ） TU528 A 1000-4637 2012 02-45-04 0 前言 为深入的研究，但对于喷射补偿收缩钢纤维混凝土 在煤矿建设与支护中，喷射混凝土是一种应用 这种新型复合材料的研究却很少见。 本课题组崔朋 很多的材料。 普通混凝土的脆性显著，安全性低，为 [6] 勃得出 ，与膨胀剂掺量为 、 、 、 的喷射补 0