接地网放热焊研究-材料科学与工程专业论文.docxVIP

万 万方数据 Abstract Title: RESEARCH ON EXOTHERMIC WELDING OF GROUNDING GRID Major: Material Physics and Chemistry Name: Xinhua LI Signature: 白比ìrl Supervisor: Prof. Lajun FENG Signatu阳 L4LNM Abstract Substation groundintgrid is a major measure that to ensure the normal operation of electrical equipment and personal safety. But the welded joint of grounding grid is often an important part of the corrosion. How to ensu民 the safety of the joint connecting of grounding grid，small corrosion and heat has bee? the focus of attention in transmission line project. Domestic grounding grid widely used the galvanized steel. In this work，based on the grounding grid material in the domestic to develop a exothermic welding powder that apply to the galvanized steel and copper- clad steel grounding material. And using the stretching，four-probe tester，DSC，SEM，and other methods to study the effects of electrochemical workstation exothermic welding powder particle size and all components welded joint appearance on section，字 tensile strength，DC resistance ， corrosion resistance ，thermodynamics properties ，microstructure. The results show that when the particle size of exothermic welding powder is more than 120mesh，the reaction was violent and had a 1町ge splash，the security of reaction was low. When the p町ticle size of solder pow?er is less than 120mesh，the reaction was difficult to ignite. When the p町ticle size of solder powder is 120mesh，the reaction was gentle，splash less，high safety and had the best performance. In the exothermic welding powder of galvanized steel grounding material ，with the increasing of Al content，the tensile strength and DC resistance of welded joints had decreased. When the content of Al is 20wt.%，the pores and inclusions of appearance and 仕acture surfacè of joints were least. The corrosion rate of joint metal was only O.012623mm!a and the microstructure of weld was formation. The alloying agent of Cu has different effects on weld tensile st