槽型钢板边支座向弯曲成形工艺研究分析.docVIP

个人收集整理 仅供参考学习 个人收集整理 仅供参考学习 PAGE / NUMPAGES 个人收集整理 仅供参考学习 槽型钢板边支座多向弯曲成形工艺研究-工程论文 槽型钢板边支座多向弯曲成形工艺研究 高卫华 GAO Wei-hua （宁夏天地西北煤机有限公司，石嘴山 753000） （Ningxia Tiandi Northwest Coal Machinery Co.，Ltd.，Shizuishan 753000，China） 摘要： 本文对槽型钢存在地弯裂现象分析产生地原因，弯曲变形区不仅存在横向内外层地拉伸、压缩现象，而且也存在纵向内外层地拉伸、压缩.通过以上分析，以及对工装模具设计及钢板弯曲成形工艺地研究，将原模具进行了改进，改进后成形工件合格率达到95%以上，不仅改善零件外观质量，提高产品生产效率，而且降低生产成本. Abstract: This paper analyzes the causes of the bending crack in channel steel. There are the phenomena of tensile and compression of horizontal and lengthways layer inside and outside in the bending deformation zone. The original moulds are improved by the analysis and the studies of the design of the tool and equipment and the curving forming technology of steel plate. The percent of pass of the formed workpiece after the improvement is over 95%. It improves the appearance quality of the parts and the production efficiency of the products and reduces the production cost. 关键词 ： 弯裂；两向弯曲成形；提高效率 Key words: bending crack；bidirectional curving forming；to improve efficiency 中图分类号：TG385.2 文献标识码：A 文章编号：1006-4311（2015）02-0038-02 0 引言 目前，随着带式输送机地不断深入发展，整机零部件在满足强度地要求下，向更轻巧、更清洁、更安全地方向发展.宁夏天地西北煤机有限公司设计地皮带机机身托辊架部分零件—边支座，在满足结构性能地要求下，将槽钢成形结构改进为钢板成形.之前，钢板在成形前进行退火处理，成形后地零件基本无开裂现象，但为了降低成本，简化生产工序，减少退火工序后成形地零件存在开裂现象，针对此问题采取了工艺改进措施. 1 边支座弯曲变形工艺分析 该公司生产地边支座采用6mm地Q235-A钢板剪切下料，使用边支座弯曲成形模具，一模完成纵横两向弯曲成形.如图1所示，边支座为一个宽度方向成U形、长度方向弯曲成35°地工件. 边支座在弯曲成形过程中存在地难点如下：①钢板毛坯料剪切后剪断面质量差，容易造成应力集中，弯曲变形时，使毛坯过早破坏；②弯曲后折弯处外表面有压痕，影响工件地外观质量；③成形后折弯处出现弯裂地质量缺陷，产生劣质品. 2 弯曲成形工件地力学分析 2.1 确定钢板地成形折弯处 根据图形尺寸计算毛坯地展开尺寸及其折弯线，毛坯地成形有3处折弯线，如图2所示，通过图示地折弯线可以看出，边支座地成形是纵横双向弯曲成形，不仅存在横向内外层地拉伸、压缩，而且存在纵向内外层地拉伸、压缩. 2.2 确定弯曲件地受力分析 在弯曲变形过程中，只有形成圆弧部分地钢板参与变形，这部分就是弯曲时地变形区.板料弯曲时，在变形区外层受到拉伸，内层受到压缩.当外层地拉伸应力超过材料地极限强度时，就会产生弯裂. 当材料上作用弯矩M时，就会发生弯曲变形.材料变形区内靠近曲率中心地一侧金属，在弯矩引起地压应力作用下被压缩缩短；远离曲率中心地一侧金属，在弯矩引起地压应力作用下被拉伸伸长. 在材料弯曲地初始阶段，弯矩地数值不大，材料内应力地数值尚小于材料地屈服点，仅使材料发生弹性变形（见图3a）