高露洁漱口水对不锈钢托槽抗腐蚀性的影响王婧1王璞1高静1张.DOCVIP

高露洁漱口水对不锈钢托槽抗腐蚀性的影响 王婧1，王璞1，高静1，张旭1，张凯亮2，曹宝成1 （730000 兰州；兰州大学：口腔医学院口腔正畸科1；口腔医学院颌面外科2） [摘要]目的 研究高露洁漱口水对不锈钢托槽抗腐蚀性的影响，为临床工作提供指导。方法 将三种不锈钢托槽分组，浸泡于高露洁漱口水中10d，提取浸提液，检测离子析出量，观察金属托槽表面形貌。用极化曲线法检测电化学腐蚀现象。 结果 1.离子析出：经方差分析，3B托槽组中的铁、锰、铬离子析出量最高；镍离子析出量依次为：3B新亚ORJ；ORJ组中的铜离子析出量大于新亚（P＜0.05）。2.扫描电镜：浸泡前，ORJ、3B托槽槽沟表面较粗糙，新亚托槽表面较光滑。浸泡后，3B托槽表面腐蚀最严重。3.动电位极化曲线：三组托槽中，新亚托槽的自腐蚀电位最小，ORJ托槽的自腐蚀电流密度最大。结论 高露洁漱口水对ORJ、3B托槽的抗腐蚀影响较大，对新亚托槽影响较小。 [关键词]高露洁漱口水；不锈钢托槽；抗腐蚀性；离子析出；电化学 [中图法分类号 ] R783.5 [文献标志码] A Corrosion resistance of 3 stainless steel brackets in Colgate mouthwash Wang Jing1, Wang Pu1, Gao Jing1,Zhang Xu1，Zhang Kailiang2 ,Cao Baocheng1 (1Department of Orthodontics，School of Stomatology,2Department of maxillofacial surgery,School of Stomatology，Lanzhou University,Lanzhou,Gansu Province, 730000, China) [Abstract] Objective Study the?corrosion?resistance?of?the?metal brackets were caused by Colgate, to?provide guidance for clinica. Methods The stainless steel bra -ckets were soaked in Colgate mouthwash.To extact the extractions after 10 days.The atomic absorption spectrometer and observe the surface of the brackets before or after immersion by scanning electron microscopy.Petentiodynamic polarization technique was used to depict polarization curve and to measured the electric potential of corro -sion(Ecorr) and the current desity of corrosion(Icorr) of three brands of brackets in the [基金项目] 中央高校基本科研业务费专项资金(lzujbky-2012-161)；甘肃省自然科学基金(1208RJZA236)。 [通信作者］曹宝成，E-mail:caobch@ Colgate. Results 1.ion release: for 1-way analysis of barianc(ANOVA),the level of iron, manganese and chromium of 3B brackets was significantly higher than ORJ and xinya; the level of of nickel release was in the following order: 3B ?xinyaORJ;While the copper release between ORJ and xinya was significantly different（P＜0.05）,the level of ORJ was higher than xinya. 2.The SEM comfirmed?the sureface structure in 3B after immersion was much severely than before.3.Potentiodynamic polarization curve: The Ecoors of xinya wer