含碳化物奥铁体球墨铸铁磨球新型热处理工艺及磨球失效机理研究-材料加工工程专业论文.docxVIP

含碳化物奥 含碳化物奥铁体球墨铸铁磨球新型热处理工艺及磨球失效机理研究 河北工业 河北工业大学硕士学位论文 RESEARCH ON NEW HEAT-TREATMENT TECHNOLOGY AND FAILURE MECHANISM OF CADI GRINDING BALL ABSTRACT Carbidic austempered ductile iron，so-called CADI，is a new kind of wear resistant material that derived from ADI in recent years.It has a good application and prospect in Metallugical and Mine Industries.This work focuses on the research of new-heat treatment technology and failure mechanism of CADI grinding ball. It mainly includes: 1) Research on cooling capacity of salt-bath quenching medium； 2) Determination of the heat-transfer coefficient between the CADI thermal probe and the salt； 3) Experimental investigation of the new heat-treatment technology on CADI grinding ball； 4) Stress numerical simulation of CADI grinding ball during the falling sphere test；5) Research on failure mechanism of CADI grinding ball. The result showed: 1) In the test range(0~2%)，as water in the salt-bath increased，the cooling capacity of the salt was intensified at the same temperature ； In the test range(250℃~350℃)，the cooling capacity of the salt weakened at the same temperature as the austempering temperature enhanced； 2) The cooling curves of the quenching medium can not display the surface information of the thermal probe，but it has special uses；3) The heat-transfer coefficient between the CADI thermal probe and the salt was determined under the one-dimensional heat transfer model by ANSYS program and the result was reliable； 4) The temperature field of the CADI grinding ball during the austempering was simulated by ANSYS program and the necessary time for the balance of the temperature field was derived； 5) In the test range(4min~150min)，as the salt-bath austempering time increased，the hardenability of the CADI grinding ball enhanced while the hardness and impact toughness of the ball showed the same trend；6)In the new heat-treatment test，the mechanical properties of the φ100mm CADI grinding ball with the salt-bath austempering t