不同脱敏剂对牙本质小管的封闭作用及对牙本质粘接强度的影响研究.docVIP

不同脱敏剂对牙本质小管的封闭作用及对牙本质粘接强度的影 响研究 ［ ］目的探讨不同脱敏剂对牙本质小管的封闭作用及对牙 本质粘接强度的影响。方法选择新鲜拔除无嶠坏人磨牙172 颗，44颗用于封闭作用实验，128颗用于牙本质粘结强度实验, 4°C生理盐水保存。制备牙本质试件、粘接试件，测试微拉伸粘 接强度，观察脱敏效果、亚甲基蓝溶液渗透法结果、微拉伸粘接 强度。结果①封闭作用实验：空白对照组：磨切之后玷污层将 强度。 结果①封闭作用实验：空白对照组：磨切之后玷污层将 牙本质的表面覆盖，牙本质小管多数由玷污层封闭o Hybrid Coat 组：牙本质表面平坦，牙本质小管被完全封闭。Gluma组：牙本 质表面平坦，牙本质小管被完全封闭。极固宁组：牙本质表面平 坦，牙本质小管被完全封闭。②粘接强度实验：空白对照组：亚 甲基蓝色素沿着牙本质小管渗入牙髓腔，着色较深；Hybrid Coat 组：亚甲基蓝色素渗入牙本质浅层至中层，最深处为1.4 mm； Gluma组：亚甲基蓝色素渗入牙本质浅层至中层，最深处为1?4 IIIII;极固宁组：亚甲基蓝色素渗入牙本质中层且向深层渗透，最 IIIII 深达2?3 mm。③微拉伸粘接强度测试：空白对照组、Hybrid Coat 组和Gluma组与单瓶纳米接结剂Single Bonda 2、登泰克SE Bonda的粘接强度均显著高于极固宁组(P0. 05),极固宁组显 著降低粘接强度，差异有统计学意义(P〈0?05)。结论Hybrid Coat及Gluma脱敏剂对全酸蚀及自酸蚀粘接剂的粘接强度无明 显影响；极固宁处理可显著降低全酸蚀及自酸蚀粘接剂的粘接强 度。 ［关键词］脱敏剂；牙本质小管；封闭作用；牙本质粘接强 度；影响 ［ ］R783. 3 ［ ］B ［ ］ 1673-9701 (2016) 24-0054-03 ［Abstract］ Objective To investigate the sealing effect of different desensitizer on dentinal tubule and the influence on the bond strength of dentine? Methods 172 molars without caries were newly removed and 44 were used for the sealing experiments and 128 were used for the dentinal adhesive st reng th experimen ts and all the molars were res to red in the normal saline at 4°C? The dentinal samples were prepared, the samples were adhered, the micro-tensile bond strengths were measured , and the desensitized effects , the methylene blue solution infiltration resuIts and the micro-tensile bond strengths were observed? Results The blank control group: the surface of the dentine was covered by the smear layer after the incision and the most dentinal tubule was seen mostly sealed by the smear layer. Hybrid Coat group： The surface of the dentine was flat and the dentinal tubule was completely sealed? Blank control group: The methylene blue solution was infiltrated into the dental pulp cavity along the dentinal tubule and the dye was relatively deeper； Hybrid Coat group： The methylene blue solution was infiltrated into the surface to the middle layer of the dentine and the deepest part was 1. 4 mm； Gluma