超高强度钢板Docol1200M温弯曲回弹研究-精密成形工程.PDF

摇摇摇 44 精 密 成 形 工 程摇 摇 摇 2013年3月 超高强度钢板Docol1200M温弯曲回弹研究 赵阳,伍玉琴,刘斌,段磊 (重庆理工大学 重庆市模具工程技术研究中心,重庆400054) 摘要:根据弯曲试验的原理设计并制造了模具,通过物理实验得出超高强度钢板Docol1200M在不同温 度下V形弯曲和U形弯曲时的回弹,通过对实验结果的分析总结出回弹角度随温度变化的规律。 关键词:温弯曲;回弹;物理实验 DOI:10.3969/ j.issn.1674鄄6457.2013.02.010 + 中图分类号:TG386.3 1摇 摇 摇 文献标识码:A摇 摇 摇 摇 摇 文章编号:1674鄄6457(2013)02鄄0044鄄03 Research on the Spring鄄back of Ultra High Strength Steel Docol1200M with Warm Bending ZHAO Yang,WU Yu鄄qin,LIUBin,DUAN Lei (Chongqing Mold Engineering Technology Research Center,Chongqing University of Technology,Chongqing400054,China) Abstract:The moldwas designed and manufactured according totheprincipleof bendingtest,and springbackof Vbending and U鄄shaped bending forultrahighstrengthsteelplateDocol1200Munderdifferenttemperatureswasacquiredbythephysicalexperiment. The law of the springback anglewith the change of the temperaturewas summed up by the analysis of the test results. Key words:warm bending;springback;physical experiment 摇 摇 回弹是板料在冲压成形后,成形件从模具中取 笔者参照国家标准设计了实验方案,并设计制 [2] 出后产生与加载方向相反的回复现象。 当零件的回 造了模具 。 V 形弯曲采用的模具成形角度为 弹量超过产品的允许误差时,就成为缺陷,以至影响 90毅,弯曲半径为8 mm,U形弯曲模具凸模的弯曲半 [1] 产品的几何精度 。 由此可见,研究超高强度钢板成 径为8 mm,如图1,2所示。 形时的回弹对超高强钢板的成形性研究有重要意义。 1摇 温弯曲成形实验 1.1摇 实验设备及模具 摇 摇 实验时,主要利用400 kN 的曲柄压力机提供压 力,通过行程控制实验过程。 加热设备采用箱式加 热炉,利用温控设备进行温度的控制与调节,板料加 图1摇 V形弯曲模具 热后直接移至模具弯曲,然后用万能游标角度尺对 Fig.1V bending mould 弯曲件进行测量。 收稿日期:2012鄄09鄄10 作者简介:赵阳(1986-),男,河南信阳人,硕士,主要研究方向为精密塑性成形及模具。 第5卷摇 第3期摇 摇 赵阳等:超高