锰酸盐（稀土合金）锆钛酸铅铁电铁磁多层膜中的磁电效应-物理电子学专业毕业论文.docxVIP

锰酸盐(稀士合金)一锆钛酸铅铁电铁磁多层膜中的磁电效应Abstract 锰酸盐(稀士合金)一锆钛酸铅铁电铁磁多层膜中的磁电效应 Abstract Pcrovskite-type Lao．7Sr03Mn03皿SMO)powder samples were synthesized by the sol-gel method．The powder was pressed into pellets and treated with a hot-press facility．The hot-pressed samples were further sintered at 1573K to obtain dense LSMO samples with beRer magnetic parameters．PZT was first poled by heating to 425K and cooling back to room temperature in an electric field of 30～50kV／em perpendicular to the sample plane．Then both planes of PZT were painted by silver electrode．LSMO—PZT bilayers jvere bonded by slow-dry epoxy resin with hardener． The structure of LSMO samples was represented by x-ray diffraction(XRD)．The morphology Was observed through scanning electronic microscopy(SEM)．It Was found that the stacking density of hot pressed LSMO Was larger than that of the not hot pressed one．The magnetization Was measured by a vibrating sample magnetometer．The bilayers exhibited superior ME coupling compared to thick-fill composites prepared by tape casting process．The transverse coupling is stronger than the longitudinal interactions and a maximum in the ME voltage coefficient Was measfired at H=1 500e．The voltage coefficients were then measured as the疗equeney f of the ac field 61-1 was varied．Upon increasing￡aE．31 increased gradually with minor peaks at 80kHz and 170kHz，and received a maximum of 1300mV／cm Oe at 268kHz．There is exceHent agreement between theory and the ME data measurement． In order to adapt to the requirement of the practical application，on the basis of results of previous work，we simplified the experimental equipment，improved the sensitivity of the sample，and did fnrther research of the ME effect in laminate compositesofTbl-xDyxFevy-Pb(Zr,Ti)03(TDF-PZT)drivenby singlemagneticfield． The PZT powder made by chemical method Was pressed into disks of lOmm in diameter and lmm in thickness．．The disks then were sintered at different temperatures from 1000。C to 1200 oC to obtain PZT s