镧铈混合掺杂纳米TiO2的制备及光催化性能研究材料加工工程专业论文.docxVIP

重庆大学硕士学位论文英文摘要 重庆大学硕士学位论文 英文摘要 PAGE PAGE IV TiO2 nanotubes can be prepared by microwave. TiO2 nanotubes are open, hollow tube, almost the same diameter by observed in the electron microscope, the outer diameter of La-Ce co-doped TiO2 nanotubes is 10-15nm, the inner diameter is 4-8nm, and the length is about 50-80nm. 3. To methyl orange as target degradation, the nanopowder and nanotube are studied about photocatalytic by the 15W UV light irradiation at 150min, the result show that La-Ce co-doped improves the photocatalytic activity of TiO2 nanoparticles and nanotubes. The high activity is due to the strong absorption of UV-visible range, the formation of oxygen hole, the enhanced adsorption capacity and so on. Key words: rare earth , co-doped , TiO2 , photocatalytic property 重庆大学硕士学位论文目 重庆大学硕士学位论文 目 录 目 录 中文摘要 I 英文摘要II 1 绪 论 1 1.1 引言 1 1.2 稀土掺杂纳米 TiO2 的概况 1 1.2.1 稀土的特性 2 1.2.2 稀土掺杂 TiO2 纳米粉的制备 2 1.2.3 掺杂对 TiO2 光催化活性的影响 4 1.3 TiO2 纳米管的制备及应用 6 1.3.1 纳米管较粉体的优点 6 1.3.2 TiO2 纳米管的制备 7 1.3.3 TiO2 纳米管的形成机理 8 1.3.4 TiO2 纳米管光催化反应的基本原理 9 1.4 纳米 TiO2 光催化剂的改进 10 1.4.1 贵金属沉积 10 1.4.2 复合半导体 11 1.4.3 稀土元素掺杂 11 1.4.4 过渡元素掺杂 11 1.4.5 表面还原处理 12 1.5 本文的研究目的和主要研究内容 12 1.5.1 本文的研究目的 12 1.5.2 本文的研究任务 12 1.5.3 本研究的技术路线 13 2 镧铈混合掺杂 TiO2 纳米粉的制备及表征 14 2.1 试剂与仪器 14 2.2 混合掺杂 TiO2 纳米粉的制备方法 15 2.2.1 制备溶胶 15 2.2.2 干凝胶的制备 15 2.2.3 热处理工艺 15 2.2.4 研磨过筛 15 2.3 表征与分析 15 2.3.1 形貌分析 15 2.3.2 结构分析 18 2.3.3 TiO2 纳米粉体形成机理 22 2.4 本章小结 26 3 镧铈混合掺杂 TiO2 纳米管的制备及表征 27 3.1 试剂与仪器 27 3.2 混合掺杂 TiO2 纳米管的制备方法 27 3.3 试验结果与评价 28 3.3.1 形貌表征 28 3.3.2 结构表征 29 3.4 本章小结 32 4 镧铈混合掺杂纳米 TiO2 的光催化性能 33 4.1 引言 33 4.2 实验方法 33 4.2.1 试剂与仪器 33 4.2.2 光催化反应装置 34 4.2.3 试验方法 34 4.3 结果与分析 35 4.3.1 暗态试验结果与分析 35 4.3.2 空白试验结果与分析 36 4.3.3 镧铈混合掺杂纳米 TiO2 的光催化性能研究 36 4.4 镧铈混合掺杂纳米 TiO2 提高光催化性能机理研究 39 4.5 本章小结 43 5 结论与展望 45 5.1 结论 45 5.2 展望 45 致 谢 47 参考文献 48 附 录 53 重庆大学硕士学位论文1 重庆大学硕士学位论文 1 绪 论 PAGE PAGE