钢铁化学成分.docVIP

钢号 化学成分（%） 机械性能（≥） 　 　 C Si Mn P≤ S≤ Cr Ni Mo Cu V σb MPa σb MPa δ％ Ψ ％ HB AKv J 碳 钢 铸 件 ZG200-400 ≤0.20 ≤0.50 ≤0.80 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 400 200 25 40 　 30 ZG230-450 ≤0.30 ≤0.50 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 450 230 22 23 　 25 ZG270-500 ≤0.40 ≤0.50 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 500 270 18 25 　　 22 ZG310-570 ≤0.50 ≤0.60 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 570 300 15 21 　 15 ZG340-640 ≤0.60 ≤0.60 ≤0.90 0.04 0.04 ≤0.30 ≤0.30 ≤0.20 ≤0.30 ≤0.05 640 340 10 18 　 10 WCA ≤0.25 ≤0.60 ≤0.70 0.04 0.045 ≤0.50 ≤0.