起重机钢结构焊接工艺规程.docVIP

Location:Examiner or test body:Harbin Welding Training Institue 工艺编号:工艺评定编号: Welding procedure reference No.:WPAR No. : 制造商:焊工姓名: Manufacturer:Welder,s name: 焊接方法:气体保护焊135 焊接位置:平角焊 Welding process:MAG135 Welding positions:PB 接头类型:对接接头坡口制备和清理方法:机械加工或气割清磨 Joint type:butt joint Method of preparation and cleaning:Machining and grinding 母材牌号及证书:Q960E 母材厚度/规格(mm:t=12 Parent material specification:Q960E Material thickness/outside diameter(mm: 焊材类别和牌号:实芯焊丝G89 4 M Mn4Ni2CrMo 焊材特殊烘干规定: Filler metal classification and trade name:Special baking or drying: Details of backing:Details of back gouging: 预热温度:100-150℃层间温度:≤170℃ Preheat temperature:Interpass temperature:≤170℃ 焊后热处理:加热和冷却速度*: Post-weld heat treatment:Anneal Heating and cooling rates*: 其它说明* Other information* 焊丝干伸长度:15~20mm 摆动(焊道最大宽度(mm: Contact tube-to-workpiece distance:Weaving(maximum width of run (mm: 脉冲焊接情况:离子焊接情况: Pulse welding details:Plasma welding details: