d2752-88中文版-石棉纤维透气性标准试验方法.docVIP

D 2752 PAGE 1008 Designation: D 2752-88 (Reapproved 1997)编号：D2752-88（1997年重新审批） PAGE 1007 Standard Test Methods forAir Permeability of Asbestos Fibers These test methods are under the jurisdiction of ASTM Committee C-17 on Fiber-Reinforced Cement Products and are the direct responsibility of Subcommit tee C17.03 on Asbestos-Cement Sheet Products and Acessories.本试验方法归 These test methods are under the jurisdiction of ASTM Committee C-17 on Fiber-Reinforced Cement Products and are the direct responsibility of Subcommit tee C17.03 on Asbestos-Cement Sheet Products and Acessories.本试验方法归ASTM C-17纤维钢筋水泥产品委员会管辖，并由C17.03石棉水泥板产品和附件分委会直接负责。 Current edition approved May 27, 1988. Published July 1988. Originally published as D2752 - 68 T. Last previous edition D2752 - 87.现行版本于1988年5月27日批准，并于1988年7月出版。最初版本编号为 This standard is issued under the fixed designation D 2752; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (ε) indicates an editorial change since the last revision or reapproval.本标准以固定编号D 2752刊发；紧随编号后的数字表示最初采用的年份，或者是修订版的最后修订年份。圆括号中的数字表示最新重新批准的年份。上标（ε）表示自上一修订版或重新批准后的编辑性修改。 1. Scope 适用范围 1.1 These test methods cover the measurement of the relative degree of openness or degree of fiberization of milled asbestos fiber by air permeability instruments.这些试验方法涵盖通过透气仪测量精加工石棉纤维的相对稀疏度或纤维化程度。 1.2 Method A is the recommended procedure and describes a determination by means of the Rapid Surface Area apparatus. This test method is limited to fibers with an effective surface area in the range from 10 to 250dm2/g (490 to 12 000 ft2/lb).方法A为推荐程序，它描述了使用快速表面面积仪器进行测量。 1.3 Method B is an alternative procedure and covers the use of the Dyckerhoff apparatus. This test method is limited to fibers within the range from 10 to 600 Dyckerhoff seconds.方法B为可选程序，它涉及迪克霍夫仪器的使用。本试验方法限于纤维，历时10-600迪克霍夫秒。 1.4 Only th