苯乙烯-丙烯酸酯共聚物乳液在水泥砂浆中的功能.pdfVIP

Materials and Structures (2010) 43:443–451 DOI 10.1617/s11527-009-9501-3 ORIGINAL ARTICLE Function of styrene-acrylic ester copolymer latex in cement mortar Ru Wang Æ Peiming Wang Received: 3 September 2007 / Accepted: 20 April 2009 / Published online: 30 April 2009 RILEM 2009 Abstract This paper focuses on the effect of the Keywords SAE latex-modified mortar styrene-acrylic ester copolymer (SAE) latex on the Physical and mechanical properties performance of cement mortar, through studying on Shrinkage rate Water capillary adsorption the water-reduction and water-retention effects of the Anti-penetration capacity SAE latex in the mortar, and the influence of the SAE latex on the air-content and the bulk density of the fresh mortar and the bulk density, compressive and 1 Introduction flexural strengths, shrinkage rate, water capillary adsorption and anti-penetration capacity of the hard- Up to now, many effective polymer modification ened mortar. The experimental results show that the systems for cement mortar and concrete have been SAE latex has good water-reduction and water- developed and are already used in various applications retention effects in mortar. The SAE latex has also in the construction industry since the concept of polymer air entrainment effect, increasing the air content and modification for cement mortar and concrete was put reducing the bulk density of the fresh mortar. The forward before 80 years. Recently, the application of apparent bulk density and dry bulk density of the concrete-polymer composites, especially polymer- hardened mortars decrease with the increase of the modified cement mortar and concrete is expanding SAE latex/cement-ratio (m /