H2S腐蚀研究进展.pdfVIP

H S 腐蚀研究进展 2 摘要 近年来我国发现的气田均含有硫化氢、 二氧化碳等腐蚀性气体， 特别是我们 四川盆地， 含硫化氢天然气分布最广泛。 众所周知， 硫化氢腐蚀是井下油套管的 主要腐蚀类型之一。 本文简述了硫化氢的物性， 研究了硫化氢腐蚀的机理和影响 因素，并在此基础上介绍了采用缓蚀剂、涂镀层管材、根据国际标准合理选材、 电化学保护等几种国内外常用的防腐措施， 并指出了各种方法的优缺点， 最后还 探讨了硫化氢油气田腐蚀研究的热点问题及发展方向。 关键词：硫化氢腐蚀，腐蚀机理，防腐技术 ABSTRACT In recent years, the gas fields found in our country contain hydrogen sulfide, carbon dioxide and other corrosive gases,especially in the Sichuan basin, with the most extensive distribution of hydrogen sulfide gas. It is well known that the hydrogen sulfide corrosion is one of the main corrosion types of the oil casing in the well. Properties of hydrogen sulfide is described in this paper to study the hydrogen sulfide corrosion mechanism and influencing factors, and on this basis, introduces the corrosion inhibitor, coating tubing, according to international standard and reasonable material and electrochemical protection at home and abroad, several commonly used anti-corrosion measures,and points out the advantagesand disadvantagesof each method, and finally discusses the hot issues and development direction of the research on oil and gas fields of hydrogen sulfide corrosion by. Key words：hydrogen sulfide corrosion, corrosion mechanism, corrosion protection technology. 前言 随着各国经济的发展， 对石油及天然气需求进一步增加， 易开采的油气资源 已趋于枯竭，油井的发展趋势向着高技术方向发展，钻探区域势必转移向内陆、 沙漠等环境恶劣的地区。 目前我国新发现的油气田， 钻探条件恶劣， 大多均含有 硫化氢、 二氧化碳等腐蚀性气体， 特别是我们四川盆地， 含硫化氢天然气分布最 广泛。同时钻探井深增加， 4000~6000m，有的超过 7000m。高温高压： 100MPa 以上的气体的压力，井底温度达到 150℃；井下情况复杂：部分地区井下有多套 高低压地层（包括高压气层） ，多套高压盐水层，盐岩层以及存在高陡构造等情 况；新区块大多含有较为严重的腐蚀介质， 如 H2 S、CO2 。如塔里木轮南油田 CO2 含量 0.6~2.5%，分压 0.7~3.5