尾矿机制砂配制C60钢管大体积混凝土的配合比设计及应用.pdfVIP

试验研究 Experimental Research 尾矿机制砂配制C60钢管大体积混凝土的配合比 设计及应用 张全贵 北京金隅混凝土有限公司 北京 100165 摘 要：本文分析了顶升法施工钢管混凝土结构中内浇C60混凝土的特点和难点，按照用尾矿机制砂、两级配机制石 和大掺量矿物掺合料（粉煤灰、矿渣粉、硅灰）配制自密实混凝土的技术路线来设计配合比，并试验了内养护剂的减 缩功能。试验结果表明：掺加一定量的内养护剂后，C60钢管自密实大体积混凝土能够满足实际工程的质量要求。 关键词：尾矿机制砂；顶升法；钢管混凝土；内养护剂 Mix Design and Application of C60 Steel Tube Mass Concrete Prepared with Tailings Machine-made Sand Abstract: This paper analyzes the characteristics and difficulties of the cast-in-place C60 concrete in the construction of concrete-filled steel tube by the jacking method, designs the mix proportion according to the technical route of preparing self-compacting concrete with tailings machine-made sand, two-graded machine-made stone and large amount of mineral admixtures (fly ash, slag powder, silica fume), and tests the shrinkage reduction function of the internal curing agent. The test results show that after adding a certain amount of internal curing agent, C60 steel pipe self-compacting mass concrete can meet the quality requirements of practical projects. Key words: Tailings machine-made sand; jacking method; concrete filled steel tube; internal curing agent 够方便地进行浇筑，靠混凝土自重就能浇筑到模板内的 引言 [2] 各个角落，且无需进行任何振捣即能达到密实效果 。 钢管混凝土结构（Concrete-filled Steel Tube，简称 在钢管混凝土的应用过程中，尤其是施工过程中，由 CFST），是指在钢管内填充混凝土而形成的组合结构，它 于钢管内操作空间小、作业高度和强度大、施工时间长等 不仅能够更有效地发挥钢材与混凝土材料各自的优点[1] ， 因素，通常普通振捣浇筑较难实现，因此产生了新的浇筑 而且还克服了钢管结构易屈曲的缺点。相比钢结构，CFST 方法。DB11/T 1628—2019《钢管混凝土顶升法施工技术 可节省大量钢材，耐火性更好；相比混凝土结构，CFST可 规程》中第2.0.1条提到，高位抛落法（简称高抛法）和泵 获得更大的建筑空间，减少自重量，提高抗震性能等。为 送顶升法[3]所代表的无振捣浇筑方法应运而生。SCC具有 了加强钢结构的刚度，钢管内设计了大