超细涂料色浆的制备及其稳定性研究

杜长森;张明俊;宋立新;郭小春;李四伟

【摘要】Thecharacteristicsofpaintcolorants,suchascolorstrengthandfastnessarenotonlyinfluencedbythechemicalstructuresanddispersibilityofpigmentmolecules,butalsobythesizeanddistributionofparticleofpaintcolorants.Thesmallerparticlesizeofpigment,thebettercolorstrength,glossandhidingpower.Thereforedevelopmentofultra-finepaintcolorantshavereceivedincreacingconcerns.Thisarticledescribedtheprocesstomakeultra-finepaintcolorants,anddiscussedtheinfluenceofthestructureanddosageofdispersantandthetreatmenttimeandpowerofultrasoniconthepigmentdispersion,andanalysedthestabilityofcolorants.TheresultindicatedthatthedispersantFPEshowedbettereffectonpigmentdispersion.Anoptimumformulationwasasfollows;pigment15%,thedispersant20%ofpigment,thetreatmenttimeofultrasonic30minsandpower800W.Theparticlesizeofultra-finepaintcolorantscouldbe150.9nm,andthestabilityofcentrifugation93.27%.Thestabilityexperimentshowedthatthepaintcolorantsprovidedgoodstabilitytotemperature,pHandelectrolytes.%涂料色浆的着色强度和色牢度等性能除了与颜料分子的化学结构、分散性密切相关外,还与涂料色浆微观颗粒的大小与分布有关.颜料粒径越小,其着色强度、光泽和遮盖力越好,因此,超细涂料色浆的制备得到了人们越来越多的关注.本课题研究了超细涂料色浆的制备方法,讨论了分散剂结构及用量、超声波处理时间、超声波处理功率对颜料分散效果的影响,分析表征了所制备涂料色浆的稳定性.研究结果表明分散剂FPE对颜料的分散效

果较好,其较佳工艺为:颜料含量15％,分散剂用量占颜料用量的20％,超声波处理时

间30min,处理功率800W,所制备的超细涂料色浆的粒径可达到150.9nm,其离心稳定性达93.27％.稳定性实验表明所制备的涂料色浆具有良好的对温度、pH和电解质的稳定性.

【期刊名称】《涂料工业》

【年(卷),期】2012(042)003

【总页数】5页(P65-69)

【关键词】超细;色浆;制备;稳定性

【作者】杜长森;张明俊;宋立新;郭小春;李四伟

【作者单位】苏州世名科技股份有限公司,江苏昆山215337;苏州世名科技股份有限公司,江苏昆山215337;苏州世名科技股份有限公司,江苏昆山215337;苏州世名科技股份有限公司,江苏昆山215337;苏州世名科技股份有限公司,江苏昆山215337

【正文语种】中文

【中图分类】TQ628.1

与染料相比，涂料染色和印花具有显著节能减排的优势，应用前景广阔［ 1－2］。众多研究表明涂料色浆的粒径越小，其着色强度、光泽和遮盖力等越好，对提高涂料色浆的应用性能至关重要。迄今为止，减小颜料颗粒大小、提高涂料色浆在水性体系中分散稳定性的方法很多，如松香处理法、涂料衍生物法、有机胺类处理法、添加分散剂法、等离子体处理法、超微离子吸附法等。

添加分散剂法是颜料分散和稳定最为广泛且效果较好的一种方法。钱国坻等［3］

采用低分子分散剂亚甲基双甲基萘磺酸盐在砂磨机