钢渣细集料的水化状态与有关性能研究.pdfVIP

2007 中国钢铁年会论文集 钢渣细集料的水化状态与有关性能研究 方宏辉 王 悦 祝 斌 （武钢研究院） 摘 要 本文讨论钢渣细集料配制胶结材的水化状态、有关性能及工程应用。试验将钢渣细集料与复合矿渣微粉组 成胶结材，掺入砂、石配制成混凝土，按照水泥强度检验方法，探索强度变化规律，测定胶结材和混凝土在各种条 件下的表现特征，观察微观结构，分析影响因素，检验工程应用状况。 关键词 钢渣细集料 复合矿渣微粉 胶结材 混凝土 Research on Hydrating Condition and Capacity of Steel-Slag Fine Aggregate Fang Honghui Wang Yue Zhu Bin (RD WISCO) Abstract This article discusses the hydrating condition, capacity and application of steel-slag fine aggregate used in cementitious matter. in the experiment, the cementitious matter composed of steel-slag fine aggregate and compound micro slag powder mix the sand and macadam into the concrete. Refer to the test method of cement intensity, explore the intensity law, measure the behavior characteristics terms under various formula, observe the microstructure, analysis the factor of the influencing, and check the application on project. Key words steel-slag fine aggregate, compound micro slag powder, cementitious matter, concrete 中国钢铁渣堆弃量约 3 亿 t[1], 占地 3 万亩。2005 年钢铁渣的产生量为 1.65 亿 t[2] ，综合利用率为 50 ％。其中高炉矿渣产生量为 1.15 亿t ，综合利用率为65 ％。钢渣的产生量为5000 万t ，综合利用率为10 ％。无论从资源与能源方面考虑或就环境保护而言，工业渣的综合利用都列为国内外的重要课题。钢铁 渣在工业废渣中占有较大比重，用作建筑材料是处理大量钢铁渣的有效途径，因而在建材资源中有重要 的地位。 为探索钢渣细集料及混凝土的水化特性，获得较致密的水化凝聚结构，使混凝土具有良好的物理力 学性能，根据国内外学者的研究成果，进行了钢渣细集料复合矿渣微粉胶结材的研究，发现钢渣细集料 与复合矿渣微粉组成胶结材具有异常良好的性能，并将其配制成混凝土用于工程建筑，初步取得了较为 满意的结果。 1 原料与试验 1.1 原料 钢渣细集料为磁选后粒径小于 5mm 的自然级配渣，现场处理后直接使用，表观密度约2.85t/m3 。岩相 鉴定钢渣主要矿物组成为 C S、C S、RO 相、Ca （OH ）、铁酸盐以及少量的磷灰石和游离氧化钙等。复合 3 2 2 矿渣微粉主要以高炉水渣及石膏调节料和组合料组成，比表面积大于350m2 3