含粗骨料的超高性能混凝土抗压强度值的影响因素研究.docVIP

  Influences on Compressive Strength of Ultra-High Performance Concrete Incorporating Coarse Aggregate# YANG Juan1, PENG Gaifei1, GAO Yuxin2, WANG Bin2** 5 10 15 20 25 30 35 40 (1. Civil Engineering Architecture School, Beijing Jiaotong University, Beijing 100044; 2. Chengdu China Construction Ready Mixed Concrete Co., Ltd, ChengDu 610052) Abstract: In this paper, Ultra-high performance concrete (UHPC) incorporating coarse aggregate was prepared with common raw materials. An experimantal investigation was conducted on the influencing factors on compressive strength of ultra-high performance concrete, including water to binder ratio (W/B), particle size range of coarse aggregate, fine modulus of sand, dosage of binder materials, types and dosage of mineral admixtures, steel fiber. The results indicated that, all the factors tested affected compressive strength of concrete, especially the W/B and mineral admixtures. With the lower W/B, incorporating mineral admixtures and using high-performance superplasticizer, UHPC incorporating coarse aggregate can be prepared successfully with the compressive strength about 150MPa. Further research results on the mechanical properties of UHPC will be reported recently. Keywords: Ultra-high performance concrete; coarse aggregate; compressive strength 0 Introduction Ultra-high performance concrete (UHPC) has been increasingly researched and shows a very promising future in practical engineering due to its excellent properties, i.e. ultra-high strength and super-high durability. Normally, UHPC may include two types, reactive power concrete (RPC) and concrete incorporating coarse aggregate with the compressive strength of more than 100 MPa [1] UHPC has attracted more and more research attention all over the world recently [2-3]. In Japan, a 59-story residential tower was the first engineering structure of the UHPC about 150 MPa [4] successful outcomes [6]. UHPC about 100 MPa was successfully applied in construction of the Guangz