磁控退火对钴基非晶合金磁电和力学性能的影响.docVIP

  Evolution of Electromagnetic and Mechnical Properties of Co-rich Amorphous Alloys under Field Annealing# SONG Yujun1, SUN Qiangqiang1, TANG Zhaowei1, ZHANG Tao1, JIANG Yanwei2* 5 10 15 20 25 (1. Key Laboratory of Aerospace Materials and Performance, School of Materials Science and Engineering, Beihang University, Beijing 100191; 2. Key Laboratory of Fundamental Science for National Defense of Novel Inertial Instrument Navigation System Technology, Beihang University, Beijing 100191) Abstract: Microstructure changes of the cross-section of Co-rich amorphous ribbons (Co68.15Fe4.35Si12.5B15, atomic%) annealed at 450°C for 30 minutes with a 10 Oe longitudinal or transverse external magnetic field have investigated by comparing with those as spun and annealed samples without field. The ribbons annealed under the transverse field exhibit an extremely distinct gradient microstructure across the section of the ribbon (gradient nano-amorphous ribbons), featured with the amorphous-phased skin layers (top and bottom) of about 4-5 μm and one middle crystalline layer of about 10-12μm having the grain size of 434 ± 99 nm. While the ribbons annealed under the longitudinal field are featured by formation of primary nanocrystals with size of 2.5 ± 0.4 nm and inter-grain spacing of 2.0 ± 0.5 nm almost uniform dispersing in the amorphous residues (nano-amorphous ribbons). These kinds of amorphous-nanostructural composites preserve unique magnetic properties and enhanced conductivities by comparing with those as-spun ribbons or annealed ribbons without field, leading to excellent giant magneto-impedance (GMI) effects. Particularly, the nano-amorphous ribbons lose the dual-peak feature as the as-spun ribbons but a mono GMI peak, and preserve a maximum MI ratio of 520 % at a given frequency of 10MHz and the maximum field of 40Oe. While the gradient nano-amorphous ribbons still show dual-peak feature as the as-spun ribbons, preserve a sensitivity of 200 %/Oe at the low magnetic fi