使用化学溶液沉积制备Fe掺杂的YBCO薄膜.docVIP

  Fe doped epitaxial YBCO films prepared by chemical solution deposition# Zhang Hong, Wang Wentao, Zhao Yong** 5 10 15 20 25 30 35 40 (Superconductivity RD Center, Southwest Jiaotong University, Chengdu 610031) Abstract: YBCO coated conductor has wide prospect in large scale application. But low current carrying capability restrain the practical application of YBCO coated conductor at high temperatures and high magnetic fields. Therefor, It is crucial for the preparation of theYBCO coated conductor with high critical current density. In this paper, epitaxial, dense, smooth and crack-free Fe doped YBCO films were prepared on LaAlO3 (LAO) single crystal substrate via a fluorine-free polymer-assisted metal organic deposition (PA-MOD) method. The effects of Fe doping on microstructure and superconducting character of YBCO films were investigated. The critical temperature for superconducting of the Fe doped YBCO film degrades slightly. However, In-field critical current density of YBCO films improves with this dilute Fe doping, except the doping quantity x = 0.005 compare to the pure YBCO film. Therefore, the current carring capability of YBCO film can improve through doping appropriate Fe in to the YBCO. It means that Fe doping in YBCO film may be a feasible way to prepare high performance conted conductor. Keywords: superconductivity physics; YBCO films; doped 0 Introduction Recently, worldwide attention has been paid to the preparation of YBa2Cu3O7-δ (YBCO)-based coated conductors i.e. the second generation tapes because of its wide prospect in large scale application [1-7]. The major approaches of fabricating YBCO coated conductors include in situ processes like PLD, magnetic sputtering and etc as well as ex situ wet chemistry approaches. In view of the fact that chemical solution deposition (CSD) and related techniques are of great interest because they provide versatile and cost-effective processing routes with controlled stoichiometry and microstructure, it i