精密合金冷轧钢带分层缺陷原因研究.docVIP

精密合金冷轧钢带分层缺陷原因研究 任福全1，2 薛庆国2 陈军1 王静松2 （1，北京北冶功能材料有限公司，北京100192）（2，北京科技大学，北京100083） 摘要：本文针对精密合金冷轧钢带中存在的分层缺陷问题展开研究。通过对分层缺陷取样进行能谱分析，确定了Al2O3等非金属夹杂物是造成冷轧钢带分层的主要原因。提出工艺改进措施。 关键词：钢带分层 夹杂 扫描电镜 Abstract The lamination defects of cold rolled strip of precision alloy are researched in this paper. Steel ingots are ultrasonic tested and dissected, the lamination defects of forging stocks and cold rolled strip stocks are inspected by ultrasonic inspection, and samples are acquired from the defect locations of cold rolled strip, cold strip stock, forging stock as well as casting ingot. The test result