面向等离子体钨铜功能梯度材料的优化及服役性能研究.pptVIP

主要内容 1 2 3 4 课题提出及研究目标 研究进展 存在的不足 后续计划 后续计划 高热负荷性能研究 * * 强流脉冲离子束设备（瞬态热负荷）示意图 实验方案及样品已经准备好 实验仪器在预约等待时间中 论文成果 * * 文章成果： [1] 朱大焕，王坤，王先平，刘长松，方前锋，陈俊凌，偏滤器第一壁W/Cu FGM的热应力模拟与优化设计[J]，稀有金属材料与工程，2011.9, 40（9）1658-1661. [2] Zhu Dahuan, Liu Yang, Chen Junling, Yan Rong, Thermo-mechanical calculation on VPS-W coating used as the plasma facing materials in EAST, Plasma Science Technology(accepted). [3] ZHU Dahuan, WANG Kun, WANG Xianping, CHEN Junling, et al Residual thermal stress simulation and analysis on CVD-W coating for fusion application, The fourteen Nuclear Physics conference of China, Sep. 1-5, 2010 Hefei, Anhui [4] D. H. Zhu, J. L. Chen et al. Surface cracking behaviors of sintered ultra-fine grained tungsten under the edge plasma irradiation, nuclear fusion and plasma physics,(submit) [5] D. H. Zhu, J. L. Chen et al. Development of multi thick - layered W/Cu functionally gradient material, will submit to Journal of nuclear material,(submit) [6] 鄢容，陈俊凌，朱大焕，刘洋，EAST等离子体辐照后第一镜表面光学特性研究,核聚变与等离子体物理. [7] Liu Yang, ZHU Dahuan, Chen Junling, Zhou zhangjian, Yan Rong, Exposure of W-TiC/Cu functionally graded materials in the edge plasma of HT-7 tokamak, Plasma Science Technology. * * * * * * * * ASIPP ASIPP ASIPP ASIPP 面向等离子体钨铜功能梯度材料的优化及服役性能研究 学生：朱大焕 导师：陈俊凌 研究员 2011.12.7 中国科学院等离子体物理所博士学位论文中期检查 主要内容 1 2 3 4 课题提出及研究目标 研究进展 存在的不足 后续计划 * * 钨基PFM材料的应用优缺点 Interface cracking W CTE:4.5×10-6/K Cu CTE:17×10-6/K High heat flux Cooling water 应力“歧点” 优点： 低的溅射率 低的氚滞留 高的熔点 低的蒸汽压 高温力学性能 缺点： 低温脆性 中子辐照变脆 与热沉失配 高温重结晶 起泡，肿胀 课题提出 * * 解决方法： Castellated 结构 过渡层 ●高塑变材料 OFHC ●中间材料（热胀系 数介于钨和铜之间） W/Cu FGM * * W/Cu FGM 研究策略 课题研究方案 热-结构分析： 温度场 残余热应力 工作热应力 材料成分及结构设计 材料制备 服役行为评价 优化制备工艺技术 设计优化 * * W/Cu FGM 研究现状 设计： ● 数值计算 ● 有限元模拟 制备： ● 粉末冶金 烧结溶渗，热压烧结，熔铸-扩散，超高压烧结，放电等离子体烧结。。。 ● 涂层方法 等离子体喷涂，激光熔覆，气相沉积。。。。 性能评价： ●高热负荷性能评价 ●服役性能评价 PM-Thick layered FGM VPS-Thin layered FGM * * 研究目标 采用有限元热结构分析，针对未来稳态运行的钨铜模块界面进行