焊接热影响区断裂性能试验研究.pdfVIP

焊接热影响区断裂性能试验研究* 刘永明 张晔江 陈以一 陈扬骥 （同济大学建工系，上海，200092 ） [摘 要] 为了确定断裂分析模型的参数，本文进行了结构钢（Q235c、Q345c）焊接热影响区断裂性能试 验研究，获得了两种材料在焊接热影响区的JR 阻力曲线，采用J积分撕裂模量法建立了裂纹失稳 的失效评定图。采用两种材料分别制作了一组外形尺寸一致、初始裂纹尺寸不同的单边裂纹焊 接板，测出相应的极限拉伸应力，并和理论曲线进行了对比。 [关键词] 热影响区，JR 阻力曲线，失效评定图，弹塑性断裂 [中图分类号] TU311.3 [文献标识码]：A EXPERIMENTAL RESEARCH ON FRACTURE PERFORMANCE IN WELD HEAT-AFFECT ZONE Liu Yongming, Zhang Yejiang, Chen Yiyi, Chen Yangji (Department of Building Engineering, Tongji University, Shanghai 200092) Abstract: In order to calibrate the parameter of analytic fracture models, the experimental research of fracture performance in the weld heat-affect zone was done. The relationship curve between the resistance J integral and the value of crack extension was plotted by the test. The failure assessment diagram of instability of crack propagation was also obtained. The utmost tensile intensity of a group of welded single-edge-crack plate made of Q235c or Q345c, which were same shape and different initial crack length, was obtained and compared with the theoretic curve. Key words: heat-affect zone; JR resistance curve; failure assessment diagram; elasto-plastic fracture; 一 研究背景 二十世纪九十年代以前，工程界普遍认为钢结构具有优良的抗震性能，而作为钢结构抗 震主体的钢框架更是具有足够的延性，有很强的塑性耗能能力，这种观点在以往发生的地震 〖 〗 1 中得到了许多验证，例如墨西哥地震发生后，其震灾调查表明，钢结构建筑破坏很少 。 但 1994 年美国Northridge北岭地震和 1995 年日本Kobe神户大地震以后，人们发现钢框架结 〖 〗 2 构表现不尽如人意，出现了大量的焊接节点断裂破坏 。 对于Northridge地震和Kobe大地震震后的研究发现