粉末烧结FeCrAl多孔管环拉强度研究.pdfVIP

粉末烧结 FeCrAl 多孔管环拉强度研究 The study on ring tensile strength of powder sintered porous FeCrAl 杨保军，汤慧萍，奚正平，王建永，汪强兵，李亚宁，葛渊，王峰 Baojun Yang ，Huiping Tang ，Zhengping Xi ，Jianyong Wang ，Yaning Li ，Yuan Ge ，Feng Wang （西北有色金属研究院金属多孔材料国家重点实验室，陕西 西安，710016 ） ( State Key Laboratory of porous metal materials，Northwest Institute for Nonferrous Metal Research, Xian710016 , China ） 摘要：本文以水雾化 FeCrAl 粉末为原料，制备了不同孔隙度的 FeCrAl 多孔管，研究了不同烧 结温度和孔隙度以及预氧化处理对多孔管环拉强度的影响，结果表明，FeCrAl 多孔材料环拉的 应力应变曲线与脆性材料基本相似。烧结温度对 FeCrAl 多孔材料环拉强度影响显著，随着材料 孔隙度增大，环拉强度显著减小。 关键词：FeCrAl ；多孔材料；环拉强度； Abstract ：Different porosity FeCrAl tube was prepared by powder sintering with water atomized FeCrAl powder. The effect of the different sintered temperature,porosity and pre-oxidized on the ring tensile strength of FeCrAl porous metal were investigated. The results indicated that the stress-strain curve of porous FeCrAl was similar to that of brittlenss materials. Sintered temperature was more effective on the ring tensile strength. The ring tensile strength of porous FeCrAl decreases obviously with increasing porosity of porous FeCrAl. Keywords ：FeCrAl ；porous material ；ring tensile strength 1 前言 利用高温过滤材料(金属或陶瓷过滤材料)在高温条件下实现气体的除尘和净化 [1~2] ，能够最大程度地利用气体的物理显热，提高能源利用率，实现过程强化反应 以及气体的洁净排放，简化工艺过程，节省工艺设备投资，其中，陶瓷过滤材料应 用较为广泛，陶瓷材料的脆性、难以后续加工以及联接过程的密封等问题难以解决， 为此美国 Mott 和 Pall 公司开发了低成本的 310S、FeAl 金属间化合物、FeCrAl 等烧 结金属多孔过滤材料[3~6]代替陶瓷过滤材料，其中，FeA1 烧结金属多孔过滤材料已 成功用于美国 Southern Company 和日本 Wakamatsu 的 IGCC 半工业试验装置，但 FeAl 多孔过滤材料同样存在室温脆性，为了解决 FeAl 材料的室温脆性，大量研究 发现，添加稀土、Cr 等元素能有效的降低室温脆性[7~11]，国内外有不少文献详细报 ______________________________ 基金项目：陕西省重大科技创新项目(2007ZKC03-05)、 863重点项目(2009AA032601)资助 作者简介：杨保军，男，1980年生，工程师，西北有色金属研究院，陕西 西安710016，E-mail:ybj_99@ 通讯作者：奚正平，教授，博士生导师，电话：029E-mail:pmt-skl@ 道了相关研究成果，但主要集中于对致密材料的研究，为了进一步开展金属多孔过 滤材料代替陶瓷过滤材料的目的，本