三聚磷酸铝改善镁合金表面富镁涂层耐蚀性的研究.pdfVIP

The 6th China Corrosion Conference Investigation of the Corrosion Resistance of Mg-Rich Primer with Aluminum Tripolyphosphates Xiangyu LU, Xuhui ZHAO, Yuming TANG, Yu ZUO School of Materials Science and Engineering, Beijing University of Chemical Technology, Beijing, China Email: zuoy@mail.buct.edu.cn Abstract: The performance of a Mg-rich epoxy primer with aluminum tripolyphosphates coated AZ91D magnesium alloy was studied with Machu test, salt spray test, scanning electronic microscopy (SEM), Dy- namic potential scanning and electrochemical impedance spectroscopy (EIS). The results showed that alumi- num tripolyphosphates improved the corrosion protection performance of Mg-rich primer on AZ91D alloy by inhibiting the blisters of the primer and retarding corrosion rate of AZ91D substrate. Keywords: magnesium alloy; magnesium particles; aluminum tripolyphosphates; coating; EIS 三聚磷酸铝改善镁合金表面富镁涂层耐蚀性的研究 卢向雨，赵旭辉，唐聿明，左禹 北京化工大学材料科学与工程学院，北京，中国，100029 Email: zuoy@mail.buct.edu.cn 摘 要：本文采用Machu 测试，盐雾试验，扫描电镜(scanning electronic microscopy, SEM ) ，动电位扫 描，和电化学交流阻抗(electrochemical impedance spectroscopy, EIS)研究了防锈颜料三聚磷酸铝对AZ91 镁合金表面环氧富镁涂层的影响。结果表明三聚磷酸铝可以有效抑制富镁涂层起泡现象，减缓镁合金 基体的腐蚀速率，增强富镁涂层对镁合金的防护作用。 关键词：镁合金；镁粉；三聚磷酸铝；涂层；阻抗 泼，与水极易反应生成氢气，导致富镁涂层易起泡失效。 1 引言 三聚磷酸铝作为无毒，高效的防锈颜料应用越来越广 镁合金由于其密度小、比强度高及可铸性好等特 泛。在富锌底漆配方中添加三聚磷酸铝可以减少锌粉的 点，在航空、航天和汽车等行业中有着广泛的应用前景。 用量、降低锌粉过高的活性，减少锌盐的生成，也使之 然而镁合金的耐蚀性较差，目前只少量地应用于工作环 具有复合防腐的效果。因此本研究采用三聚磷酸防锈颜 境并不恶劣的地方，其巨大潜能并没有充分发挥出来 料加入富镁涂层中，研究其对镁合金表面富镁涂层耐久 [1-3]，因此提高镁合金的耐蚀性至关重要。