高砷铅阳极泥选择性脱砷实验研究 覃小龙，谢兆凤，刘万里，谭霖 （郴州市金贵银业股份有限公司，湖南郴州 423038） 摘要：对高砷铅阳极泥进行碱性体系通入空气脱砷试验，详细考察了碱用量、空气流量、脱除温度和反应时间对脱砷率的影响。结果表明，在氢氧化钠用量为1.4倍理论量、空气流量100 L/h、液固比5∶1、温度80 ℃、阳极泥粒度0.15~0.178 mm、脱除时间2 h的最佳条件下，脱砷率达到95%以上。 关键词：高砷铅阳极泥；选择性；脱砷 中图分类号：TF812 文献标志码：A 文章编号：1007-7545（2014）05-0000-00 Experimental Study on Selective Arsenic Removal from High Arsenic Bearing Lead Anode Slime QIN Xiao-long, XIE Zhao-feng, LIU Wan-li, TAN Lin (Chenzhou Jingui Silver Industry Co. Ltd, Chenzhou 423038, Hunan, China) Abstract: Selective arsenic removal from high arsenic bearing lead anode slime was conducted in alkaline system by feeding air. The effects of dosage of caustic soda, air flow, leaching temperature and time on arsenic removing rate were investigated. The results show that the arsenic removing rate is 95% above under the optimum conditions including dosage of caustic soda of 1.4 times of theoretical value, air flow of 100 L/h, ratio of liquid to solid of 5∶1, leaching temperature of 80 ℃, size of anode slime of 0.15~0.178 mm, and leaching duration of 2 h. Key words: high arsenic bearing lead anode slime; selective; arsenic removal 从铅阳极泥中回收金银等有价金属通常采用的都是火法工艺[1-2]。某公司炼铅工艺采用“SKS”法，在铅冶炼过程中产生的铅阳极泥及外购铅阳极泥因砷在冶炼过程中不断富集已达到8%~10%。每年自产及外购处理铅阳极泥达0.5 万tAs2O3+6OH-+O2=2AsO43-+3H2O （1） As2O5+6OH-=2AsO43-+3H2O （2） 2M3(AsO3)x+6xOH-+xO2=2xAsO43-+3xH2O+3M2Ox↓ （3） 2M3(AsO4)x+6xOH-=2xAsO43-+3xH2O+3M2Ox↓ （4） 按照预定的液固比量取一定体积的自来水放入烧杯，将其置于恒温水浴槽中加热至定温度，待温度恒定后加入定粒度的阳极泥，在恒定的搅拌速度下通入一定流量的空气开始反应。达到时间后，液固分离，滤渣用80 ℃自来水100 mL洗涤次，分别计量洗水和滤液的体积取样分析As、Sb、Pb含量；滤饼在0 ℃干燥后称重取样分析 As、Sb、Pb含量。2013-10-22 基金项目：国家科技支撑计划项目（2012BAE06B06） 作者简介：覃小龙(1983-)，男，湖南常德人，工程师. 3 试验结果与讨论 3.1 氢氧化钠用量对脱砷率的影响 固定条件：阳极泥粒径为原始粒径、空气流量0 L/h、温度80 ℃、液固比1、时间2 h，氢氧化钠用量对脱率的影响 图用量对脱率的影响的影响、温度80 ℃、液固比1、时间2 h，空气流量脱率的影响 图对脱率的影响的影响空气流量0 L/h、温度80 ℃、脱率的影响 图对脱率的影响Fig.3 Effect of ratio of liquid to solid on arsenic removing rate 由于增大液固比可以改善搅拌效果，但降低了设备的利用率。液固比对脱除过程的影响较为复杂。随着液固比的增加，脱除剂和脱除液中目标元素的浓度均随之减小。由图3可见，当液固比由4∶1提高至9∶1时，脱砷率由9