炭黑表面微观粗糙度的分形研究.pdfVIP

The 6th China Corrosion Conference An Investigation on the Surface Roughness of Carbon Black by the Way of Fractal Geometry Jian CHEN College of Material Science and Chemical Engineering Sichuan University of Science and Engineering, Zigong, Sichuan, 643000 Abstract: One of the most important factors of reinforced rubber is the surface microstructure of carbon black. This paper takes observations the situation of carbon black in DFM mode of Scanning Probe Microscope. Based on the parameter of each image are applied to describe the area and perimeter of the particle surface, as well as the surface fractal dimension .The surface fractal dimension based on slit island method and the fractal box dimension (FBD).The fractal dimension value of carbon black aggregates from 1.5 to 1.6 and its particles value from1 to 1.1.It is have a good correlation with oil absorption value. The surface fractal dimension is the most effective reflect the surface character. For observation on the micro- structure of carbon black as a rational expression of the surface roughness of carbon black. Keywords: Carbon black; Fractal dimension; Scanning probe microscope 炭黑表面微观粗糙度的分形研究 陈建 四川理工学院材料与化学工程学院，四川自贡，643000 摘 要：炭黑的表面特征是其补强性能的三大因素之一，一般系用氮吸附、吸油值等表征，但新开发 的高结构炭黑定伸拉力，湿地抓力，滚动阻力等性能同时得到改善，这是传统经典理论无法解释的， 必须要寻找新的参数来表征，本文利用扫描探针显微镜（SPM ）的DFM 模式对炭黑表面形貌进行观 察，得到炭黑表面形貌图，用分形的方法进行表面分形，分形采用了盒子法和小岛法，计算相应的炭 黑粒子面积和周长得出炭黑粒子表面的分形维数。结果表明：炭黑单个粒子的分数维在 1~1.1 之间， 炭黑聚集体的分维数在 1.5~1.6 之间，这与