原油储罐钢在不同酸性盐介质中耐蚀性能的研究.pdfVIP

The 6th China Corrosion Conference Study on Corrosion Resistance of Crude Oil Storage Tank in Different Acid Salt Solution Fangfang AI, Xiaolian XU, Yiqing CHEN, Bin ZHONG, Lin LI, Peng GAO, Hong WANG Technology Center of Angang Steel Co., Ltd., Anshan 114009, Liaoning, China Abstract: Corrosion resistance of crude oil storage tank steel in four kinds of acid salt solutions was investigated in simulated practical environment by corrosion potential, linear polarization, and immersion test. The results show that compared with AH32，corrosion resistance of the steel is more excellent in acid and neutral salt solution. Especially in strong acid salt solution, the steel is of good corrosion resistance. Corrosion rate of the steel is only quarter to one-third of that of AH32. Keywords: corrosion potential; linear polarization; immersion test 原油储罐钢在不同酸性盐介质中耐蚀性能的研究 艾芳芳，徐小连，陈义庆，钟彬，李琳，高鹏，王红 鞍钢股份有限公司技术中心，辽宁，鞍山，114009 摘 要：模拟原油储罐腐蚀环境，采用自腐蚀电位、线性极化和浸泡试验考察了在不同酸性盐环境中， 3 种不同型号原油储罐钢的耐蚀性能。结果表明：在酸性和中性盐条件下，原油储罐钢耐腐蚀性能优 于对比材料，特别在强酸性盐介质环境下，原油储罐钢表现出优良的耐腐蚀性能，腐蚀速率仅是对比 材料的 1/4~1/3。 关键词：自腐蚀电位；线性极化；浸泡试验 1 前言 法考察了在不同酸性盐介质环境中原油储罐用钢的耐 蚀性能，并结合模拟原油储罐环境浸泡试验来考察原 近年，石油工业快速发展，应用储罐的量持续增 油储罐钢的耐蚀性能，进而分析合金元素对腐蚀性能 加，因在服役过程中经常受到各种有害介质的腐蚀而 的影响。 导致的安全运行问题日益突出。油品本身并不腐蚀金 属材质，但原油中含有一些腐蚀性杂质，如无机盐、 2 试验方法 硫化物、氮化物、有机酸、氧、二氧化硫和水分等， 2.1 试验材料 这些杂质溶入沉积水中，构成酸性氛围，危害性很大。 另外，随着国外原油的大量进口，尤其是中东的原油 实验材料为 3 组实验室研制的原油储罐钢和对比 占进口比例日益增加，呈高酸、高硫、高含水量变化 材料，主要化学成分见表 1。试样加工尺寸为(60 ± 趋势，更加重了油罐内的腐蚀。 1)mm×(