某难浸金矿次氯酸钠浸出的研究.docVIP

某难浸金矿的次氯酸钠浸出研究 杨聪，晋克勤，唐道文，王锐 （贵州大学 材料与冶金学院，贵阳 550025） 摘要：采用次氯酸钠某难浸金矿浸出次氯酸钠。结果表明次氯酸钠不仅可氧化分解矿石中的FeAsSFeS2，同时可打开包裹金；在金浸出率可达到75%以上次氯酸钠浓度0.6 mol/L，pH 1314，液固比6，35 ℃浸出4 h。 关键词：难浸金矿；次氯酸钠；浸出Leaching of Refractory Gold Ore with Sodium Hypochlorite YANG Cong, JIN Ke-qin, TANG Dao-wen, WANG Rui (College of Materials and Metallurgical, Guizhou University, Guiyang 550025, China) Abstract: One refractory gold ore in Guizhou Province was leached with sodium hypochlorite. The effects of concentration of sodium hypochlorite, leaching time and temperature on leaching rate of gold were investigated. The results show that sodium hypochlorite not only oxidizes FeAsS and FeS2 in gold ore, but also opens the encapsulated gold. The leaching rate of gold is above 75% under the following optimum conditions including concentration of sodium hypochlorite of 0.6 mol/L, pH of 13~14, ratio of liquid to solid of 6, leaching time of 4 h, and temperature of 35 ℃. Key words: refractory gold ore; sodium hypochlorite; leaching 在我国贵州，广泛分布着微细粒、高砷高硫的难浸金矿[1]，金以自然金的形式呈微细粒包体嵌布于载体矿物FeAsS、FeS2中，即使细磨也无法将其解离，因而金的浸出率较低，仅为15%左右。 现阶段，国内外处理难浸金矿的方法主要是高温焙烧法[2]，湿法化学氧化法[3-4]和细菌氧化法[5]，它们应用于不同的矿石，在生产中各有利弊。次氯酸钠浸金技术作为一种无污染、浸出率较高的浸金新工艺已逐步引起人们的重视。本文探索了在碱性条件下用次氯酸钠溶液浸出贵州难浸金矿石的工艺参数。 1 次氯酸钠浸金的原理 次氯酸钠是一种强氧化剂，在常温下就能分解放出O2，新生氧原子具有强氧化性，能使包裹金的硫化矿物和砷化物氧化分解[6]，分解的硫元素以SO42-存在于溶液中，砷以Na3AsO4形式存在于溶液中，化学反应式为： (1) (2) 毛暗章[7-8]等分析了金在NaClO强碱体系中的热力学行为，当体系中pH增大时，会生成Au(OH)3沉淀，pH继续增加时，Au(OH)3表现出两性，形成H2AuO3-和HAuO32-溶解于溶液中，当pH13时，金主要以H2AuO3-和HAuO32-形式存在，其机理为： (3) (4) (5) (6) 收稿日期：2012-10-08 基金项目：贵州省科学技术基金项目（黔科合J字[2010]2003) 作者简介：杨聪(1987)，男，山东枣庄人，研究生因此，在足够的碱性条件下，NaClO能将FeAsS、FeS2和Au同时浸出，将氧化破坏载金硫化矿的预处理与金的浸出两步工艺合而为一，缩短了浸金的流程。 2 试验部分 2.1 试验原料 试验所用样品贵州黔西南某金矿，金品位15.03 g/t主要成分 S 1.65、Fe 2.12、As 1.33、CaO 25.60、MgO 15.50、SiO2 8.28。矿石呈灰色、致密块状。该矿中金主要以超显微状态分散在微细硫化矿物和毒砂中，而这些载金矿物本身的粒度也很微细且含金量不稳定，还伴生大量的白云石和硅酸盐矿物，属极难选冶的大型超微细浸染型金矿。 2.2 试剂与设备 分析纯次氯酸钠，6%活性氯，8%游离碱；粒状分析纯氢氧化钠DF—101Z型恒温加热磁力搅