海洋平台用特厚A514GrQ钢种的研制.docVIP

海洋平台用特厚A514GrQ钢种的研制 高照海, 唐郑磊, 许少普， 崔冠军 (南阳汉冶特钢有限责任公司钢研所 河南南阳474500) 摘 要：阐述了152mm特厚海洋平台齿条用A514GrQ钢板在南阳汉冶特钢采用100t转炉—模铸—3800mm轧机—热处理的工艺研制开发过程，通过合理地确定化学成分、冶炼和浇铸工艺、轧制及热处理工艺，最终确保了152mm厚A514GrQ钢种保一级探伤、保力学性能的成功研制，并实现了批量化生产。 关键词：特厚板，海洋平台用钢，A514GrQ Offshore steel with extra-thick A514GrQ Development Gao zhaohai, Tang zhenglei, Xu shaopu, Cui guanjun （Iron and Steel Research Institute of NanYang HanYe Special Steel Co．Ltd．NanYang, HeNan , China,474500Abstract: The 152mm thick steel offshore platform rack with A514GrQ steel used in the Nanyang Chinese rule 100t converter - Molded-3800mm mill - heat treatment process research and development process, through reasonable to determine the chemical composition, smelting and casting process, rolling system and the heat treatment process, and ultimately ensure the protection of steel 152mm thick A514GrQ level testing, mechanical properties ensure the successful development and implementation of mass production. Keywords: special plate; offshore steel; A514GrQ 1 前言 ? A514 GrQ是ASTM标准下的经淬火与回火的高强度可焊接钢板，主要用在需要高抗拉，高屈服的场所，各类石油井架、起重吊车、高温风机、大型电铲、自卸车及钻机、煤矿液压支架、钢结构等。海洋平台用具有高强度高韧性低脆性转变温度良好的抗疲劳性能冷成型性能和焊接性能具有较好的搞腐蚀性能和一定的耐磨性能。 A514 GrQ钢化学成分（wt%） 范围 C Si Mn P S Nb Ti Mo V Cr Ni 最小 0.14 0.15 0.95 ≤0.035 ≤0.035 / / 0.40 0.03 1.00 1.20 最大 0.21 0.35 1.30 0.60 0.08 1.50 1.50 2.2 冶炼方法 采用转炉+炉外精炼冶炼。( 2.3 钢板的力学及工艺性能（见表2） 表2 A514GrQ钢板力学及工艺性能 规格/mm 室温拉伸试验 冲击试验 断面收缩率 抗拉强度Rm/（Mpa） 屈服强度ReL/( Mpa) 伸长率A/% V型冲击功Akv/J（-40℃） ≥50% 152 690～895 ≥620 ≥16 ≥46 2.4 钢板交货状态 钢板以淬火+回火状态交货，并逐张进行超声波探伤检查。 3 A514GrQ研发方案 3.1 成分设计 海洋平台用钢是通过低碳当量成分设计及控轧控冷+调质生产工艺，生产出大厚度结构用高强度调质钢，金相组织为保持马氏体位向的索氏体钢。应用强化机制为组织强化、细晶强化、析出强化和固溶强化。C主要与其他元素形成碳化物，起组织强化和析出强化的作用，使钢板强度增加； Mn主要起固溶强化和降低相变温度，提高钢板强度的作用；为了有效通过控轧工艺实现钢板结晶强化，须加入Nb元素，以提高钢板再结晶温度，加热固溶Nb阻止奥氏体晶粒长大，冷却时高温析出Nb的C、N化物；通过两阶段控轧后，V的C、N化物析出，强烈提高钢板的强度；Ni：主要作用是增大奥氏体的过冷度，从而细化组织，取得强化效果，另外还能增加钢的耐大气腐蚀能力，提高低温冲击韧性和降低冷脆转变温度；杂质元素P、S等含量下限不做限制，在工艺设备能力下尽可能降低，以达到钢质纯净、力学性能均匀的目的[1]。其设计成分见表3 表3 A514 GrQ钢内控化学成分（wt%） 规格 范围 C Si Mn P S Nb Ti Mo