商品混凝土裂缝的原因与防治探析.docVIP

商品混凝土裂缝的原因与防治探析 　　摘要：商品混凝土，又称预拌混凝土，由于其具有环保型、质量稳定性、有益于提高功效等特点已广泛的应用于土木工程。由于受施工材料、设计条件、施工技术、养护技术等多方面的影响，商品混凝土较易出现裂缝表现，直接影响建筑物的使用性能。因此，施工队伍必须不断提高施工预控技术，减少裂缝出现。本文分析了商品混凝土裂缝的出现原因，并介绍了预防裂缝的技术。 　　关键词：商品混凝土；裂缝；防治 　　Abstract: the concrete products, also called ready-mixed concrete, due to its many advantages such as environmental protection, quality stability, the effect is beneficial to improve characteristics have been widely applied in civil engineering. Due to the condition of construction materials, the design, construction technology, curing technology and other aspects, the influence of commercial concrete cracking performance, more easily direct influence on the performance of the building use. Therefore, the construction team must constantly improve the construction precontrol technology, reduce the cracks appear. This article analyzed the reasons of the cracking of concrete products, and introduces the technology of preventing crack. 　　Keywords: concrete products; Fracture; The prevention and treatment of 　　中图分类号：文献标识码：A文章编号：2095-2104(2013) 　　一、商品混凝土裂缝的原因 　　（一）商品混凝土材料 　　商品混凝土是一种由粗、细骨料（砂、石）、水泥、水及其他掺合料和外加剂混合而成的非均质脆性材料，由于混凝土的组成材料，微观构造以及所受外界影响的不同，混凝土裂缝的原因就很多： 　　1、不同型号的水泥的含碱量不同，水泥中的碱与活性骨料中的活性氧化硅起反应，形成胶状物质，从周围吸水膨胀而产生裂缝； 　　2、混凝土采用的粗细骨料级配不连续，造成混凝土的坍落度控制不到位，为混凝土裂缝的形成埋下了隐患； 　　3、矿粉作为新外加剂材料得到了应用，根据试验研究表明，矿粉等量取代部分水泥时，混凝土早期强度根据其掺量，３天、７天近似线性降低，28天、60天强度，当掺量30％以下时，变化不大，随掺量升至30％时，才升至最高。掺入矿粉的混凝土早期强度来的较慢（根据工程资料显示，28天的强度才基本达到75％），真正达到设计强度要到近两个月后。 　　（二）设计方面 　　提高混凝土强度，减少配筋。建筑设计不合理会导致混凝土结构中出现楼板裂缝，主要表现在：因结构中的断面突变导致应力集中所产生的构件裂缝；对构件施加预应力不当造成构件的裂缝；构造钢筋配置过 　　少或过粗等引起构件裂缝；未充分考虑混凝土构件的收缩变形。 　　混凝土在硬化过程中，由于水分蒸发、体积逐渐缩小，产生收缩，而板的四周由于受到支座的约束，不能自由伸展，当混凝土的收缩所引起板的约束应力超过一定程度时，必然引起现浇板的开裂。 　　（三）施工工艺 　　在混凝土结构浇注过程中,如果施工工艺不合理、施工质量低劣,容易产生各种形式的裂缝,特别是细长薄壁结构。裂缝出现的部位和走向、裂缝宽度因产生的原因而异,比较常见的有: 　　1、混凝土浇注过快,混凝土流动性较低,容易在浇注数小时后发生前述的塑性收缩裂缝; 　　2、拌和不均匀（特别是掺用掺合料的混凝土），搅拌时间不足或过长，拌和后到浇筑时间间隔过长，易产生裂缝。 　　3、连续浇筑时间过长，接茬处理不当，易产生裂缝。 　　4、高空浇注混凝土，风速过大、烈日暴晒，混凝土收缩值大。 　　（四）混凝土养护不当。 　　1、过早养护会影响混凝土的胶结能力。 　　2、过迟养护，由于受