高强度结构钢Q550D的研发实践.pdfVIP

高强度结构钢Q550D的研发实践 李忠波，高照海，李亮亮，袁永旗，于飒 (河南省南阳汉冶特钢有限责任公司技术中心钢研所 河南南阳 474500) 摘 要：本文叙述了南阳汉冶特钢Q550D高强度结构钢的研制开发过程。成分设计采用低碳高锰添加适量Mo、Ni、Nb、 Ti等合金元素，炼钢工艺采用铁水脱S预处理、LF+VD炉外精炼、低过热度浇注，轧制方面通过确定合理的加热温 度、TMCP轧制工艺、轧后堆垛缓冷等一些列工艺及措施，工业化生产出来的钢板力学性能优良、内部质量良好。 关键词：Q550D，贝氏体，TMCP，研发实践 The Development Practice in High Strength Structural Steel Q550D LI Zhong-bo ， GAO Zhaohai ， LI Liangliang， Yuan Yongqi，YU Sa (Iron and Steel Research Institute of NanYang HanYe Special Steel Co ．Ltd． NanYang, HeNan , China, 474500) Abstract: This article describes the development of high strength structural steel Q550D. In composition design, we adopted the scheme of low carbon and high manganese and added proper amount of microalloy elements, such as Mo ，Ni, Nb and Ti . In steelmaking, we adopted the processes of hot metal desulphurization, LF+VD secondary refining and low superheat casting. In rolling, we determined the proper heating temperature and adopted the proces ses of TMCP and stacking cooling. We produced the steel plates with excellent mechanical properties and internal soundness. Key words ： Q550D ；Bainite；TMCP ；Development practice 1、前言 [1,2] 低碳贝氏体钢是实现高强、高韧同时具备良好焊接性能的最具潜力钢种 ，与普通低合金钢相 比，低碳贝氏体钢板由于碳含量的大幅度降低，在保证钢板高强度的同时仍能保证很高的韧性。高 强度结构钢Q550D是一种微合金化低碳贝氏体钢，它具有强度高、低温韧性优良、焊接性能好等特点， 主要应用在使用环境恶劣的煤矿机械行业。南阳汉冶特钢有限公司在2008年新投产了3800mm轧机， 该轧机设备先进，轧制力达80000KN。通过优化微合金元素成分设计和TMCP轧制工艺，采用细晶强化、 位错强化、沉淀析出强化和控制组织相变细化相变产物等手段，成功开发出适合用户使用的低合金 高强度钢Q550D。本文通过研究不同加热温度、中间坯厚度、终轧温度、返红温度等重要工艺参数对 钢板组织和性能的影响，从而得出了生产该钢板的最佳工艺方案。 2、试验材料及试验方法 2.1化学成分设计及生产工艺流程 组织决定性能，而成分决定组织，因此要想开发出性能优异的高强度结构钢Q550D，合理的成分 设计是最基本的条件之一。在开发初期我厂在生产Q460C的基础上，通过增加微合金元素V、Nb的含 量并适当添加Mo、Ni等贵重合金，但是钢板强度很难达到550Mpa级别。所有高强度结构钢Q550D组织 必须以贝氏体组织为主，在成分设计上与常规铁素体珠光体钢有着本质上的区别，成分设计原则如 下：①降低C碳含量，抑制