提高高碳钢盘条氧化铁皮剥落性研究的论文.pdfVIP

提高高碳钢盘条氧化铁皮剥落性研究 ·1 · 提高高碳钢盘条氧化铁皮剥落性研究 1 2 1 1 2 2 2 郭大勇 任玉辉 王秉喜 高 航 车 安 孙 浩 张 欢 （1. 鞍钢股份技术中心, 鞍山 114001; 2. 鞍钢股份线材厂, 鞍山 114001 ） 摘 要 为提高高碳钢盘条氧化铁皮剥落性，对不同轧制和吐丝温度条件下的盘条氧化铁皮成分、重量百分比和厚 度等性质进行了生产试验研究。采用氧化铁形成热力学和生长动力学分析了轧制和吐丝温度对盘条氧化铁皮性质的 影响，提出了提高盘条氧化铁皮剥落性的措施。通过本文的工作，提高了鞍钢高碳钢盘条氧化铁皮剥落性，满足了 用户的使用要求。 Improvement of Descaling Properties of High Carbon Wire Rod Guo Dayong1 Ren Yuhui2 Wang Bingxi1 Gao Hang1 Che An2 Sun Hao2 Zhang Huan2 (1. Ansteel Technology Center, Anshan, 114001; 2. Wire Rod Plant of Ansteel, Anshan, 114001) Abstract In this paper, scale composition, weight percentages and thickness of high carbon steel wire rod were investigated under different laying head temperature in order to improve the descaling property of high carbon wire rod. Effects of laying head temperature on scale properties were studied by using thermodynamics and kinetics of scale formation and growth. The works of this paper provides technological supports for industrial practices. The requirement of customers is satisfied. 高碳钢盘条的氧化铁皮在包装运输过程中起到保护作用，防止盘条直接与大气接触而氧化腐蚀。盘条 在大气中形成的氧化腐蚀层，在用户的除鳞过程中不易去除，严重影响高碳钢盘条的表面质量。盘条表面 的氧化铁皮在用户使用前还必须去除，一般使用酸洗法除鳞或机械法除鳞。使用酸洗法，应使盘条氧化铁 皮量少，这样可以缩短酸洗除鳞时间。使用机械除鳞法希望铁皮量比酸洗法多一些，盘条的氧化铁皮厚， 可以使盘条在反复弯曲过程中，铁皮呈现块状，快速脱落。较薄的氧化铁皮在盘条反复弯曲过程中，呈现 粉状脱落。盘条除鳞后表面残余氧化铁皮多，导致盘条除鳞不净，不利于用户在高碳钢丝生产过程中的拉 拔和镀锌。 鞍钢线材厂在生产高碳钢盘条过程中，出现了部分批次盘条的氧化铁皮剥落性不能满足用户机械除鳞要 求的现象，在盘条除鳞过程中，铁皮呈现粉状脱落，盘条表面残余氧化铁皮多。为此开展了提高高碳钢盘条 氧化铁皮剥落性的研究工作。 高碳钢盘条轧制和吐丝温度对盘条氧化现象有重要影响，为了满足用户对高碳钢盘条氧化铁皮的性质要 求，本文采用氧化铁形成热力学和生长动力学分析了盘条轧制和吐丝温度对氧化铁皮性质的影响。通过研究 提出了改进盘条氧化铁皮剥落性的措施，满足了用户的使用要求。 ·2 ·