扬迪与MacTM+矿烧结性能的对比分析和探讨.pdfVIP

扬迪与 MacTM 矿烧结性能的对比分析和探讨 刘晓明 张艳允 郭兰芬 贾文君 王金龙 （河北钢铁集团邯钢公司技术中心，邯郸 056015 ） 摘 要 本文对同属澳系褐铁矿中扬迪和 MacTM 矿粉的烧损特性、基础特性及单烧试验结果进行了对比分析，并 对两种矿的合理使用进行了探讨。 关键词 烧损特性 基础特性 单烧特性 Comparative Analysis and Discuss on Sintering Characteristic of Yangdi Ore and MacTM Ore Liu Xiaoming Zhang Yanyun Guo Lanfen Jia Wenjun Wang Jinlong (Technique Center , Handan Iron and Steel Company , Hebei Iron and Steel Group, Handan, 056015) Abstract In the paper, experiments of the burning loss and the basic characteristics and sintering of yangdi ore and MacTM ore were introduced , then the experiment characteristic of the two ores was compared and analyzed. On the basic of experiment result, reasonable application of the two ores was discussed. Key words the characteristic of burning loss, the basic characteristics, the characteristic of sintering 1 引言 扬迪矿和 MacTM 矿来自澳大利亚 BHP Billiton 铁矿公司，虽然前者属于布鲁克曼矿，后者属于马拉曼巴 矿，但两者均为带状沉积岩的原始富集而形成的假象赤铁矿和针铁矿的组织结构，属于褐铁矿。 烧结生产中，褐铁矿由于品位低、爆烈性强、造球阶段需增加水量，甚至有些认为会增加燃料比，因此， 长期以来，褐铁矿不被认为是烧结生产中深受欢迎的矿种。随着国际市场铁矿资源价格的不断飙升，利润空 间被进一步压缩的钢铁企业不得不把调整原料结构作为降本增效的手段，从而，价格低廉、同化性能突出、 烧后品位高等特点，使褐铁矿越来越多地被作为烧结生产的主要矿种之一。 虽然两种褐铁矿都是带状沉积岩经历了长期的原始富集而形成，但是后期的地质作用决定了扬迪矿和 TM TM Mac 矿具有不同的矿物组成和结构。本文对扬迪和 Mac 矿从烧损特征、基础特性及单烧性能三个方面 进行了试验，试验结果表明两种矿在烧结过程中的表现行为不尽相同。因此，全面把握两种铁矿石的烧结特 性，对褐铁矿烧结具有积极的指导作用。 2 烧损特性 褐铁矿主要成分为针铁矿，是一种水合铁氧化物（FeOOH ），焙烧后失去部分结晶水而形成质地疏松的 组织结构，有利于提高矿石的反应活性。扬迪和 MacTM 矿是产自澳大利亚 BHP Billiton 铁矿公司的褐铁矿， 因其开采的矿点不同而具有不同的理化性能，表 1 为两种铁矿石的化学分析。从表 1 中可见，两种矿都有较 大的烧损，扬迪矿比 MacTM 矿还要高约 4.5 ％。 8-936 第八届（2011 ）中国钢铁年会论文集 表 1 扬迪和 MacTM 矿的化学成分 矿种 TFe SiO CaO MgO Al O P S FeO TiO 烧损 2 2 3